牌号简介 About |
---|
玻璃纤维增强聚酯模塑料非常好的机械强度,非常好的电气性能和尺寸稳定性,良好的磨损稳定性,高阻燃性和低烟毒性(经RATP批准),出色的加工性能-为自动加工优化主要应用:恒温器外壳,开关柜TCH零件、继电器本产品符合重金属和PCA的允许上限,也符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)的要求。 Glass-fibre reinforced Polyester moulding compound Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance together with low fume toxicity (RATP approved), outstanding processability - optimised for automatic processing Primary application(s): Thermostat housings, Switch parts, Relays This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.90 到 2.10 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 到 0.85 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate 2 |
|||
MD MD 2 |
0.20 到 0.45 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
< 0.30 | % | ISO 62 |
后收缩 Post contraction 3 |
< 0.050 | % | ISO 2577 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
注塑成型 injection molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:50~100℃ MD:50~100℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1461 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.10 mm 1.10 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
3 168 h / 110°C |
【新闻资讯】查看全部
宝理塑料: 电动汽车和信息通讯机遇处处
2018-04-25 宝理塑料是领先全球的热塑性工程塑料供应商,以“环‘宝’理念.绿色城市”为主题,展出最先进的材料技术和新的环保应用。琳琅满目的产品系列包括DURACON聚甲醛(POM)的最新进展、DURANEX聚对苯二甲酸丁二醇酯(PBT)、DURAFIDE聚苯硫醚(PPS)、LAPEROS液晶聚合物(LCP)、以及环烯烃共聚物TOPAS(COC)树脂。产品应用于新能源汽车、高端电气设备、食品和健康等多个行业。这些产品充份显示,橡塑发展也可以很环保、可持续发展,而且可减少环境足迹。 “如果从 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |