牌号简介 About |
---|
Smoothblend® PC-1201是一种耐磨聚碳酸酯化合物,通过结合聚四氟乙烯和碳纤维提供卓越的润滑性。它是为要求严格耐磨和低摩擦性能的应用而开发的。 Smoothblend® PC-1201 is a wear resistance polycarbonate compound offering superb lubricity by incorporating PTFE and carbon fiber. It is developed for applications demanding stringent wear resistant and low friction performance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.20 到 0.40 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
120 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.5 | % | ASTM D638 |
弯曲模量 Bending modulus |
10500 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与钢 - 动态 Steel - Dynamic |
ASTM D1894 | ||
与钢 - 静态 Steel - Static |
ASTM D1894 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中科大研制超弹性全碳材料
2021-09-05 搜料网资讯: 近日,中国科学院院士、中国科学技术大学教授俞书宏团队研制出一种兼具高度可压缩性和可拉伸性的超弹性全碳多孔材料,被称为碳弹簧。 该工作提供了一种用于构筑新 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |