牌号简介 About |
---|
这一等级具有优良的流动性能和高冲击强度和刚度的良好结合。它广泛用于需要良好加工性、高韧性和低翘曲性的物品,例如真空吸尘器外壳、大尺寸花盆、食品容器和冰淇淋容器。本文所述产品尤其未经测试,因此未经验证可用于医药/医疗应用。 This grade has excellent flow properties and a good combination of high impact strength and stiffness. It is widely used in articles where good processability, high toughness and a low warpage are required, e.g. vacuum-cleaner housings, large size flower pots, foodstuff containers and ice-cream containers. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
37 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃ -20℃ |
5.0 | kJ/m² | |
0℃ 0℃ |
7.0 | kJ/m² | |
23℃ 23℃ |
11 | kJ/m² | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-20℃ -20℃ |
J/m | ASTM D256-A | |
0℃ 0℃ |
J/m | ASTM D256-A | |
23℃ 23℃ |
J/m | ASTM D256-A | |
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525,ISO 306/A120 6 6 | |
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 7 7 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
1% 正割 1% secant 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 2.0 in/min |
4 testbar 80*10*4mm |
5 标准 B (120°C/h), 压 力1 (10N) |
6 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
长玻纤增强尼龙改性塑料在汽车范畴的使用
2018-01-18 尼龙是一种性能优良的工程塑料,具有优异的力学性能,突出的耐腐蚀、耐油性、耐热性、高模量等优点。对其进行增强、阻燃改性,可以显著提高其耐热性、模量尺寸稳定性及阻燃性,尼龙改性塑料广泛应用于汽车、电子电气、电动工具等行业。长玻纤增强是尼龙改性常用的一种手段。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |