牌号简介 About |
---|
Polycomp 6019是一种填充聚四氟乙烯的中到低流量聚丙烯均聚物化合物。它已被开发用于涉及饮用水的应用中,需要极低的摩擦系数。 POLYCOMP 6019 is a PTFE filled medium to low flow polypropylene homopolymer compound. It has been developed for applications involving potable water where an extremely low co-efficient of friction is required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
4.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
1.5 到 1.9 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
3 mm 3 mm 2 |
29.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂,3 mm Fracture, 3 mm 2 |
100 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
3 mm 3 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3mm 3mm |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3 mm 3 mm |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.0 mm 0.45 MPa, unannealed, 3.0 mm |
℃ | ASTM D648 |
备注 |
---|
2. 50 mm/min |
【新闻资讯】查看全部
几种降低塑料本钱的方法引见
2016-08-16 填充降低塑料的成本是指在树脂中加入成本低廉的填料,或称为填加剂。常用的填料主要为天然矿物及工业废渣等,此外还有木粉及果壳粉等有机填料及废热固性塑料粉等。填料是塑料助剂中应用最广泛,消耗量最大的一类助剂。 塑料填充的目的对于热塑性塑料,主要是降低成本;对于热固性塑料是降低成本与改性兼而有之。填充除降低成本外,不可以改善制品的某些性能。普遍可以改善的有刚性、耐热性(无机填料)、尺寸稳定性、降低成型收缩率及抗蠕变性等;有的还可以改善绝缘性、阻燃性、消烟性及隔音性等。 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |