牌号简介 About |
---|
TIPELIN® 7300B是一种高密度双峰聚乙烯共聚物(以丁烯-1为共聚单体),适用于高刚度、高抗环境应力开裂(ESCR)产品的吹塑成型,该级产品含有抗氧化剂和酸性清除剂。推荐应用TIPELIN® 7300B用于杰瑞罐的吹塑,用于包装联合国认证的侵蚀性工业化学品。该等级也推荐用于板材挤压。它也适用于波纹管。TIPELIN® 7300B适用于食品接触和制药包装产品的制造。该产品符合食品接触和药品法规。 TIPELIN 7300B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and excellent environmental stress crack resistance (ESCR).The grade contains antioxidant and acid scavenger. Applications TIPELIN 7300B is recommended for blow moulding of jerry cans for packaging of aggressive industrial chemicals bounded to UN certificates. The grade is recommended for sheet extrusion as well. It is suitable for corrugated pipes too. TIPELIN 7300B is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.955 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.10 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
12 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.40 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,F50 10% non-ionic detergent, F50 |
1000 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2 | |
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ISO 527-2 | |
屈服,模压成型 Yield, molding |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A120 | |
氧感应时间 Oxygen sensing time |
|||
200℃ 200℃ |
min | EN 728 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
陆地塑料净化日趋严重,采取行动要趁早
2018-06-20 如果不采取任何行动,海洋塑料污染可能在未来十年内增长三番。陶朗集团首席执行官史岱峰(Stefan Ranstrand)先生解释了饮料包装押金制和基于传感的分选回收解决方案如何能够化解这场危机。 英国政府最近发布了新的“海洋未来预测(Foresight Future of the Sea)”报告,再次将海洋塑料污染的危机呈现在世人面前,促使越来越多的人意识到海洋面临的危险,从而采取必要的行动来化解这一危机。该报告指出,废弃塑料已经占海洋垃圾总量的70%左右,从2015年至20 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |