Advanced Composites ATX889是一种复合聚丙烯产品,含有的填充物为滑石填料。 它,在北美洲有供货。 典型应用领域为:汽车行业。 特性包括: 冲击改性 高流动性 耐划伤性 Advanced Composites ATX889 is a Compounded Polypropylene product filled with talc. It is available in North America. Typical application: Automotive. Characteristics include: High Flow Impact Modified Scratch Resistant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
30 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
0.80 到 1.0 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
56 | J/m | ASTM D256 |
23℃ 23℃ |
160 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 2 |
|||
-18℃,Total Energy -18℃,Total Energy 2 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 21.7 ft/sec |
【新闻资讯】查看全部
澳大利亚努力降低塑料袋对环境的危害
2016-02-26 据报道,澳大利亚昆士兰州或与新南威尔士州联合禁塑,以降低塑料袋对环境的危害。目前在澳大利亚的8个行政区中,南澳大利亚州、塔斯马尼亚州、首都地区和北领地地区已实行禁塑令。 报道说,昆州环境厅厅长史蒂文・迈尔斯29日将与澳其他行政区的环境部门负责人一起参加圆桌会议,商讨如何减少塑料袋对海洋生物的致命影响及对环境的危害等问题。 迈尔斯表示,届时将有机会与新州环境负责人商讨两州是否联合出台禁塑令问题。两州若能联合禁塑,不仅有助于两州交界处的商家共同适应新政策,避免造 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |