牌号简介 About |
---|
Ryton® R-4-200NA和R-4-200BL 40%玻璃纤维增强聚苯硫醚化合物使用常规成型设备提供增强的机械强度和低维护成型。 Ryton® R-4-200NA and R-4-200BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and low maintenance molding using conventional molding equipment |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.68 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.50 | % | |
MD:3.2 mm MD:3.2 mm |
0.20 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.020 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
9.0 | kJ/m² | ISO 180/A |
3.2mm 3.2mm |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
3.2 mm 3.2 mm |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
-50 到 50℃ -50 to 50 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
-50 到 50℃ -50 to 50 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ||
UL温度额定值 UL temperature rating |
℃ | UL 746B | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
25 ℃,1 kHz 25 ℃,1 kHz |
ASTM D150 | ||
25 ℃,1 MHz 25 ℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
25℃,1 kHz 25℃,1 kHz |
ASTM D150 | ||
25℃,1 MHz 25℃,1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
绝缘电阻 insulation resistance 2 |
|||
90℃ 90℃ 2 |
ohms | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
泊松比 Poisson's ratio |
ISO 527 | ||
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 95%RH, 48 hr |
【新闻资讯】查看全部
20款儿童泳圈执行玩具标准 塑化剂不达标质检无一合格
2016-06-30 盛夏来临,很多家长迫不及待地带着孩子去游泳,而游泳圈成为游泳必需品。 可让沈城市民张女士不解的是,孩子使用新买的游泳圈在水里刚刚玩了一个小时,游泳圈充气嘴边缘就漏气了。 张女士称,当时在超市选购游泳圈时,游泳圈放在包装盒内并未取出,包装盒完好无损,张女士认为,游泳圈使用一个小时即出现漏气情况,应属于产品质量问题。 儿童塑料充气游泳圈被用于辅助婴幼儿及儿童洗澡或练习游泳,儿童游泳圈的质量安全为家长们关注。 近日,为评估儿童泳圈产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |