牌号简介 About |
---|
Kepital TX-11H中高粘度等级,适用于一般注塑成型,适用于需要降低磨损噪音和良好的摩擦和耐磨性而不牺牲机械性能的应用。表1 TX-11H高粘度,润滑剂包装等级。TX-11H适用于需要降低磨损噪音和良好的摩擦和耐磨性而不牺牲机械性能的应用。 Kepital® TX-11H A medium-high viscosity grade for general injection molding Suitable for uses requiring reduced wear noise and a good friction and wear resistance without sacrificing mechanical properties Kepital® TX-11H High viscosity, lubricant package grade. TX-11H is suitable for use requiring reduced wear noise, and a good friction & wear resistance without sacrificing mechanical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.40 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
|
5.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
2.0 | % | ASTM D955 |
3.0 mm 3.0 mm |
2.0 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,60% RH Equilibrium, 23 ℃, 60% RH |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:20~80℃ MD:20~80℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257,IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257,IEC 60093 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与金属 - 动态 &Metal - Dynamic |
|||
与自身 - 动态 With oneself - dynamic |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 100mm diameter |
3 10°C/min |
【新闻资讯】查看全部
2017年我国粉末涂料用聚酯树脂销量同比增长8.8%
2018-04-27 据中国化工学会涂料涂装专业委员会发布的2017年度统计初报,我国热固性粉末涂料行业整体运行情况如下: 2017年我国代表性企业的粉末涂料用聚酯树脂销量同比增长8.8%,销售额同比增长32.3%,聚酯树脂平均价格同比增加1959元/吨左右。 2017年我国代表性企业的粉末涂料用环氧树脂销量同比降低3.6%,销售额同比增长16.5%,环氧树脂平均价格同比增加2600元/吨左右。 2017年我国代表性企业的粉末涂料用TGIC固化剂销量同比增长6.9 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |