Supreme™ 028,聚烯烃塑性体(POP),是一种通过nexelene技术生产的乙烯-辛烯共聚物。Supreme™ 028在各种铸膜应用中表现良好,具有优异的密封性能和冲击强度。典型性能:优良的低密封起始温度和热粘强度,优越的冲击强度和透明度,与:美国。FDA 21 CFR 177.1520欧盟。10/2011号 Supreme™ 028, Polyolefin Plastomer (POP), is an ethylene-octene copolymer produced via Nexlene™ technology. Supreme™ 028 performs well in a wide range of various cast film applications with excellent sealing property and impact strength. Typical Performance: Excellent low seal initiation temperature and hot tack strength Superior impact strength and transparency Compiles with: US. FDA 21 CFR 177.1520 EU. No 10/2011 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.902 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
7.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | ASTM D374 |
落锤冲击 Drop hammer impact |
|||
25 µm 25 µm |
500 | g | ASTM D1709-A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
80.0 | ℃ | ASTM D1525 |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Sealing Initial Temperature Sealing Initial Temperature |
℃ | 内部方法 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
继杜邦陶氏并购后 新一轮并购案浮出水面
2016-02-25 去年两大化工巨头杜邦和陶氏化学合并成为了年度大新闻,近日重组案有了新进展。今日,“陶氏杜邦公司” 公布了意向拆分为三家独立上市公司后农业公司在美国的营运地点安排。至此,计划中的三家独立上市公司都明确了细节。 陶氏化学董事长兼首席执行官利伟诚(Andrew N. Liveris)表示,“陶氏化学与杜邦公司计划进行的农业业务合并将打造一家总部设在美国的全球领先企业,其业务规模和广度将能为世界范围内的农作物种植业者提供更优的价值与更多的选择,并抗衡全球最大的竞争对手。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |