牌号简介 About |
---|
Pellethane® 2363-80A 是一种热塑性聚氨酯弹性体,符合USP Class VI |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比重 Specific Gravity Specific Gravity |
1.12 | ASTM D792 | |
模具收缩率 Mold Shrinkage Mold Shrinkage |
0.1-0.6 | % | ASTM D-955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness Shore hardness |
80 | Shore | ASTM D224 |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
50% 拉伸 elongation 50% stretch elongation |
4.1 | MPa | ASTM D412 |
100% 拉伸 elongation 100% stretch elongation |
5.9 | MPa | ASTM D412 |
300% 拉伸 elongation 300% stretch elongation |
MPa | ASTM D412 | |
拉伸伸长率 Tensile Elongation Tensile Elongation |
% | ASTM D412 | |
拉伸强度 Tensile Strength Tensile Strength |
MPa | ASTM D412 | |
拉伸变形 Tensile set Tensile set |
% | ASTM D412 | |
撕裂强度 tear strength Tear strength |
kN/m | ASTM D624 | |
压缩永久变形 Compression Set |
|||
23℃ 23℃ |
% | ASTM D395 | |
70℃ 70℃ |
% | ASTM D395 | |
泰伯耐磨性 Taber Abrasion Taber Abrasion |
mg | ASTM D1044 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 | |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | ASTM D3418 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
陶氏新一代抗水树交联聚乙烯获R&D 100大奖
2016-01-27 德克萨斯州休斯顿――2015年1月15日――陶氏化学公司(纽约证券交易所代码:DOW)旗下的业务部门陶氏电能及信息业务部,凭借其最新一代抗水树交联聚乙烯(TR-XLPE)DOW ENDURANCE™ HFDC-4202 EC (C4202)获“R&D 100大奖”。该奖项专门用于奖励过去一年中最重要的技术创新。 该化合物所包含的专利配方技术能延长电缆寿命并提高电缆可靠性,同时降低设施所有者的系统生命周期总成本。C4202是陶氏成熟的抗水树交联聚乙烯(TR-XLPE) |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |