牌号简介 About |
---|
HANWHA LLDPE 3127采用Unipol工艺制造,设计用于层压膜。LLDPE 3127具有良好的光学性能和加工性能的平衡性。 HANWHA LLDPE 3127 is manufactured by Unipol process and designed for lamination film. LLDPE 3127 has well balanced property of optical property and processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
30 | µm | 内部方法 |
拉伸强度 tensile strength |
ASTM D882 | ||
断裂 fracture |
21.6 | MPa | ASTM D638 |
MD,断裂,30 µm MD, fracture, 30 µ m |
42.2 | MPa | ASTM D882 |
TD,断裂,30 µm TD, fracture, 30 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,30 µm MD, fracture, 30 µ m |
% | ASTM D882 | |
TD,断裂,30 µm TD, fracture, 30 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
30 µm 30 µm |
g | ASTM D1709 | |
撕裂强度 tear strength |
ASTM D1004 | ||
MD,30 µm MD,30 µm |
kN/m | ASTM D1004 | |
TD,30 µm TD,30 µm |
kN/m | ASTM D1004 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
30 µm 30 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
|||
Optimum Gage Range Optimum Gage Range |
µm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
2017年到2023年之间协作机器人的数量 年增长57%
2018-07-31 总的来说,机器人市场和协作机器人市场正在飞速发展,一份预测报告表明在2017年到2023年之间协作机器人的数量将会以惊人的57%年复合增长率增长。 协作机器人供应商Rethink Robotics(波士顿 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |