牌号简介 About |
---|
Lexan Exl1443T聚碳酸酯(PC)硅氧烷共聚物树脂是一种符合FDA和欧盟食品接触标准的注塑级树脂。与标准PC相比,该树脂具有良好的低温(30 C)延展性、中等流动特性和良好的加工性,有机会缩短IM循环时间。LEXAN™ EXL1443T resin有透明和不透明的颜色,是广泛食品接触应用的最佳候选。 LEXAN EXL1443T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1443T resin is available in transparent and opaque colors and is an excellent candidate for a broad range of food contact applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.19 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
9.50 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.40 to 0.80 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-30℃,Total Energy -30℃,Total Energy |
J | ASTM D3763 | |
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
2.50 mm 2.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 80*10*4 mm |
10 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
美利肯无色紫外线吸收剂,让PET瓶跟紫外线“拜拜”
2017-05-08 PET瓶是常见的包装容器,广泛应用于个人护理用品(洗发水、洗手液、沐浴露以及化妆品);家庭清洁用品(如清洁剂、洗手液和洗碗机剂);各种固体食物和香料;果汁和功能性饮料,以及维生素包装中。 为满足消费者的需求,品牌商不得不在上述内容物中加入人造色素和防腐剂,但由于PET瓶容易透光,紫外线可分解这些人造色素和防腐剂,容易对内容物的外观、外观,颜色,味道及营养价值产生负面影响。 尽管品牌商在产品的储藏、分销、零售展示过程中,会避免让PET瓶接受阳关和室内照明直射, |
美利肯无色紫外线吸收剂,让PET瓶跟紫外线“拜拜” PET瓶是普遍的包装材料,广泛运用于本人护理品(洗发液、洗手消毒液、沐浴乳及其护肤品);家中清洁用具(如清洁液、洗手消毒液和水槽洗碗机剂);各种各样固态食材和香辛料;水果汁和功能饮料,及其维他命包裝中。 为考虑顾客的要求,品牌商迫不得已在所述內容物中添加人工合成黑色素和添加剂,但因为PET瓶非常容易透光性,紫外线可降解性这种人工合成黑色素和添加剂,非常容易对內容物的外型、外型,色调,味儿及营养成分造成不良影响。 虽然品牌商在商品的贮藏、分销商、零售展现全过程中,会防止让PET瓶接纳阳光和室内采光照射,但这依然无法逃离无所不在的紫外线。 该怎么办? 美利肯(Milliken)在2020年的Interpack展览会上,展现了怎样根据防腐剂为PET瓶出示紫外线维护! 该吸附剂根据出示合理的紫外线过虑消化吸收,为內容物出示维护,另外还能维持包装制品的渗透性,为PET包裝产生真实使用价值! 消化吸收过虑95%的紫外线 ClearShield吸附剂可过虑95%光波长达到390纳米技术的紫外线,只需极低的使用量,便可做到合理的实际效果,让品牌商可在包裝內容物中应用大量的紫外线比较敏感食用香料和添加剂。而品牌商因为降低需要的增稠剂和添加剂,另外也可降低中药制剂的多元性,最后能够 控制成本。 减少产品成本 ClearShield已得到欧州食品安全局(EFSA)食品类触碰运用的准许,它摆脱了传统式技术性的存在的不足。ClearShield紫外线吸附剂便于解决和精确测量,它可立即添加PET中,不容易渗入饮品中。PET瓶坯的制造商根据应用添加ClearShield的PET,也可简化工艺。 完成可持续发展观 但应用ClearShield的益处远不止于此,它还能产生可持续性经济效益,“针对初创期者而言”,美利肯技术经理Simon Bousquet表述,“选用ClearShield的使用量相比传统式紫外线吸附剂的使用量降低20倍,而最后的安全防护实际效果是一样的。另外,品牌商还担心它会像一些传统式紫外线增稠剂那般含有有害化工品成份,另外还会继续对污水导致环境污染。” 除此之外,Bousquet强调:“更强的內容物维护和增加保存期,有利于降低商品消耗。因为选用了ClearShield,品牌商可再次选用纯天然、未上色的PET,防止应用深棕色或彩色的器皿来做包裝”,他表述道。“这些不全透明及有色板块的PET原材料在回收的情况下,会让回收流变性黑,使回收更为艰难,减少回收商品的使用价值。” 总公司坐落于阿姆斯特丹的欧州塑胶回收研究会(PRE)也曾保持警惕:彩色PET瓶(袋)的总数已经逐渐升高,这将为PET的将来回收产生风险。PRE进一步强调,一旦PET瓶被搜集归类以后,这种彩色的PET瓶必须再次快递分拣出去,回收站一旦售卖这种彩色PET瓶,他们历经回收解决以后,回收料可能被染上灰黑色或深灰色,再一次运用的使用价值也将受到非常大影响。 来源于:CPRJ 中国塑料硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。