牌号简介 About |
---|
Pocan DP CF 220000000 PBT+PC,非增强,注塑,阻燃,提高冲击强度,低翘曲倾向 POCAN® DPCF2200 000000 PBT+PC, non-reinforced, injection molding, flame retardant, improved impact strength, low tendency to warp POCAN® DPCF2200 000000 PBT+PC, non-reinforced, injection molding, flame retardant, improved impact strength, low tendency to warp POCAN® DPCF2200 000000 PBT+PC, non-reinforced, injection molding, flame retardant, improved impact strength, low tendency to warp |
产品描述 Product Description
厂家:德国朗盛 LANXESS
类别:PC+PBT PC+PBT
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级V-0; 低翘曲性; 阻燃; 冲击性能好; Low warping,High impact resistance,Flame Characteristics,V-0
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.80 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
15.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:250℃,2.0 mm TD:250℃,2.0 mm 2 |
0.90 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs 3 |
0.50 | % | ISO 294-4 |
MD:250℃,2.0 mm MD:250℃,2.0 mm 2 |
% | ISO 294-4 | |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs 3 |
% | ISO 294-4 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
115℃ 115℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
1.6 mm 1.6 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 7792 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2; WZ 60°C; 600 Bar |
3 60x60x2mm, 60°C MT, 600 bar |
4 60x60x2 |
5 60x60x2mm |
6 0.079 in/min |
7 Pull Rate: 2 mm/min; 50% RH |
8 2 mm/min |
9 10°C/min |
【新闻资讯】查看全部
Saipem和合作伙伴将在意大利建造碳捕集和利用工厂
2022-02-11 据俄罗斯油气网1月28日消息称,意大利承包商Saipem已经与一家合作伙伴合作,探索建设一个二氧化碳捕集和利用(CCU)工厂。 与Tenaris和Siad一样,这家能源服务公司现在将启动意大利北部 |
Saipem和合作伙伴将在意大利建造碳捕集和利用工厂 据俄罗斯油气网1月28日消息称,意大利承包商Saipem已经与一家合作伙伴合作,探索建设一个二氧化碳捕集和利用(CCU)工厂。 与Tenaris和Siad一样,这家能源服务公司现在将启动意大利北部一个脱碳设施的设计阶段。 该项目包括每天捕集30吨二氧化碳,这些二氧化碳是由安装在意大利北部TenarisDalmine工厂的热电厂产生的。 Saipem的技术允许使用废热,同时避免使用其他工艺中使用的有毒物质。三家公司之间的谅解备忘录是分阶段制定的,其中第一个阶段将是可行性研究。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 外壳控制单元
- 2019-04-11 0
- POCAN® DP CF 2200 000000是注塑成型非增强(PBT+PC)混合材料。西门子选择Pocan-DP CF2200作为自动化系统外壳,因为其具有良好的尺寸稳定性和良好的耐化学性、韧性和流动性。
- 阅读全文
外壳控制单元
1-POCAN® DP CF 2200 000000是注塑成型非增强(PBT+PC)混合材料
2-熔体体积流动速率(260℃/5.0 kg),15.0 cm³/10min
3-简支梁缺口冲击强度(23℃),10.0 kJ/m²
4-阻燃等级(0.75mm),V-0
POCAN DP CF2200是一种弹性体改性阻燃(PBT+PC)混合物,满足以下要求。其GWFI值为960°C,GWIT值为800°C,登记在美国测试公司保险商实验室(UL)的黄牌上。西门子选择Pocan-DP CF2200作为自动化系统外壳,因为其具有良好的尺寸稳定性和良好的耐化学性、韧性和流动性。Kunststoffe International提供全面的技术文章。
收起