牌号简介 About |
---|
Viton® AL-600是一种“Al族”胶聚合物,与前体Viton B-70N相比,其加工性能得到了改善。这种胶提供:更高的粘度改善了模具流动性,更好的模具释放,更少的模具污染改善了压缩永久性,以及良好的低温特性应用燃油系统,如喷油器O形环。当使用胶聚合物混合物作为织物和其他基材的溶液涂层时,O型环、垫圈和其他密封装置的注射和转移成型-挤压绳索、型材和管道或压延板。 Viton® AL-600 is an "AL-family" gum polymer that demonstrates improved processing when compared to its precursor Viton® B-70N. This gum provides: Higher viscosity Improved mold flow Better mold release Less mold fouling Improved compression set resistance, and Good low temperature characteristics Applications Fuel systems, such as fuel injectors O-rings Injection and transfer molding of O-rings, gaskets, and other sealing devices Extruded cords, profiles and tubing, or calendered sheets, when a blend of gum polymers are used Solution coatings of fabrics and other substrates. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.77 | g/cm³ | ASTM D792 |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
60 | MU | ASTM D1646 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 2 |
58 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 3 |
72 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 4 |
70 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 5 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 6 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 7 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 8 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变,23℃ 100% strain, 23 ℃ 9 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 10 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 11 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 12 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 13 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 14 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 15 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服,23℃ Yield, 23 ℃ 9 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 10 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 11 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 12 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 13 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 14 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 15 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂,23℃ Fracture, 23 ℃ 9 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 10 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 11 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 12 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 13 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 14 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 15 |
% | ASTM D412 | |
撕裂强度 tear strength 16 |
|||
23℃ 23℃ 16 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
150℃,70 hr 150℃,70 hr |
% | ASTM D395B | |
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
200℃,168 hr 200℃,168 hr |
% | ASTM D395B | |
232℃,22 hr 232℃,22 hr |
% | ASTM D395B | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积变化 Volume change |
ASTM D471 | ||
23℃,168 hr,in M15(Fuel C/Methanol 85/15) 23℃,168 hr,in M15(Fuel C/Methanol 85/15) |
% | ASTM D471 | |
200℃,70 hr,在IRM 903油中 200 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20 in/min, 老化 M15 (Fuel C/Methanol 85/15) 168 hr 在 73°F |
3 20 in/min, 老化 70 hr 在 392°F |
4 20 in/min, 老化 IRM 903 Oil 70 hr 在 392°F |
5 20 in/min, 老化 168 hr 在 392°F |
6 20 in/min, 老化 24 hr 在 450°F |
7 20 in/min, 老化 70 hr 在 482°F |
8 20 in/min, 老化 168 hr 在 482°F |
9 C 模具 |
10 老化 M15 (Fuel C/Methanol 85/15) 168 hr 在 73°F |
11 老化 70 hr 在 392°F |
12 老化 IRM 903 Oil 70 hr 在 392°F |
13 老化 168 hr 在 392°F |
14 老化 24 hr 在 450°F |
15 老化 70 hr 在 482°F |
16 老化 168 hr 在 482°F |
【新闻资讯】查看全部
盛禧奥任命Francesca Reverberi为首席可持续发展官
2021-10-09 搜料网资讯: 9月29日,盛禧奥宣布Francesca Reverberi将担任新设立的高级副总裁兼首席可持续发展官一职,立即生效。 在这个新角色中,Reverberi负责通过继续构建其可持续化学品组合并推 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |