牌号简介 About |
---|
产品描述:trexprene d50bu是一种热稳定的PP/EPDM基热塑性硫化弹性体(TPV)。这种黑色化合物主要用于发动机罩下的应用,如垫子、密封件、垫圈、风道、CVJ护套、盖子、索环或其他需要柔软性和一致性的零件。这种材料可以使用注塑、挤压、吹塑或其他熔融加工技术进行加工。 Product Description: TREXPRENE ® D50BU is a heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This Black compound is intended primarily for underhood applications such as mats, seals, gaskets, air ducts, CVJ boots, covers, grommets or other parts where softness and conformity are needed. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 to 0.960 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
TD,屈服 TD, yield 2 |
18.7 | MPa | ISO 37 |
TD,100% 应变 TD, 100% strain 2 |
13.9 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
|||
TD,断裂 TD, fracture 2 |
700 | % | ISO 37 |
撕裂强度 tear strength 3 |
|||
TD TD 3 |
91 | kN/m | ISO 34-1 |
压缩形变 Compression deformation |
|||
70℃,24 hr 70℃,24 hr 4 |
% | ISO 815 | |
70℃,24 hr 70℃,24 hr |
% | ASTM D395B | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
Brittleness Temperature(Type B) Brittleness Temperature(Type B) |
℃ | ISO 812 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
Change in Tensile Stress(125℃,70 hr,in IRM 903 Oil) Change in Tensile Stress(125℃,70 hr,in IRM 903 Oil) |
% | ISO 1817 | |
Change in Tensile Strain at Break(125℃,70 hr,in IRM 903 Oil) Change in Tensile Strain at Break(125℃,70 hr,in IRM 903 Oil) |
% | ISO 1817 | |
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
撕裂强度的变化率 Change rate of tear strength |
|||
70 hrs,in IRM 903 Oil,125℃ 70 hrs,in IRM 903 Oil,125℃ |
% | ISO 1817 | |
Change in Tensile Properties Change in Tensile Properties |
|||
Stress at 100% Elongation in Air,168 hrs:150℃ Stress at 100% Elongation in Air,168 hrs:150℃ |
% | ISO 188 | |
Stress at 100% Elongation in IRM 903 Oil,70 hrs:125℃ Stress at 100% Elongation in IRM 903 Oil,70 hrs:125℃ |
% | ISO 1817 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐臭氧性 Ozone resistance 5 |
|||
40℃ 40℃ 5 |
ISO 1431-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 100 pphm, Method A |
【新闻资讯】查看全部
研讨显示陆地塑料垃圾正在让珊瑚礁变得极易生病
2018-01-31 据外媒报道,除了饱受过度捕捞和不断上升水温之苦,珊瑚礁正在面对着来自海洋塑料垃圾对它们的伤害。根据发表第在《科学》上的一篇研究文章了解到,致使珊瑚礁患病的塑料垃圾数量已从4%上升到了89%。这是多么触目惊心的数字! 塑料袋、吸管、小玩具、快餐包装、塑料瓶等等,它们都是环境的一大问题。而海洋现在已经变成了这些垃圾的“新家”,甚至在一些非常远的海域也发现了它们的身影。 文章指出,据估算,亚太地区的珊瑚礁上发现了110多亿个塑料碎片。如果不立即采取措施,这一数字将 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |