牌号简介 About |
---|
BaydUR 646是一种用于反应注射成型(RIM)工艺的硬质聚氨酯结构发泡体系。该系统作为两种反应性液体成分提供:组分A是聚合物二苯甲烷二异氰酸酯(PMDI),组分B是不含CFC-或HCFC发泡添加剂的配方多元醇系统。BaydUR 646系统用于生产复合材料的泡沫芯,例如滑水板、尾板、雪板以及运输和海洋市场的各种部件。与任何产品一样,在给定应用中使用Baydur 646系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 Baydur 646 is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. The system is supplied as two reactive liquid components: Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The Baydur 646 system is used to produce foam cores for composite applications, such as water skis, wake boards, snow boards, and various components for the transportation and marine markets. As with any product, use of the Baydur 646 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.239 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:6.35 mm MD:6.35 mm |
0.30 到 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
内部方法 | ||
-- -- 2 |
3.8 | kJ/m² | 内部方法 |
-- -- 3 |
4.0 | kJ/m² | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
按重量计算的混合比: 110 | ||
部件 B Component B |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,6.35 mm Shaw D, 6.35 mm |
ASTM D2240 | ||
邵氏 D,12.70 mm Shore D, 12.70 mm |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
MPa | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
断裂,12.70 mm Fracture, 12.70 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
6.35 mm 6.35 mm |
MPa | ASTM D790 | |
12.70 mm 12.70 mm |
MPa | ASTM D790 | |
压缩强度 compressive strength |
ASTM D695 | ||
6.35 mm 6.35 mm |
MPa | ASTM D695 | |
12.7 mm 12.7 mm |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.5 |
3 0.25 in |
【新闻资讯】查看全部
寒冬降临 钛白粉何处“取暖”
2015-12-16 我国钛白粉市场在近十年来随着需求升级快速发展,导致盲目扩产,低端产品过剩,竞争惨烈的现状。在全球经济低迷,原油价格下挫的大环境下,钛白粉行业进入了发展低谷,转型升级是当下迫在眉睫的重要工作。 行业专家指出 |
寒冬降临 钛白粉何处“取暖” 在我国钛白粉销售市场在近十年来伴随着要求升級迅速发展趋势,造成 盲目跟风提产,中低端产品产能过剩,市场竞争激烈的现况。在全世界经济低迷,石油价格大跌的大环境下,钛白粉行业进入了发展趋势低潮期,转型升级是时下刻不容缓的关键工作中。 行业权威专家强调,在我国钛白粉产业链正处在产业结构调整、转型升级的关键期,必须搞好以下几个方面重要工作中。 1、增加技术更新改造和节能降耗技术的开发设计、营销推广和运用幅度,勤奋打造出翠绿色生态化钛白粉产业链。发展趋势翠绿色绿色经济是市场的需求网络热点,钛白粉企业要创建多层面、考虑行业具体必须的技术自主创新人才队伍建设,提高高档产品关键技术,提高資源耗能使用率,大力推广节能型、低硫、低碳环保的产品。 2、全力推动“走向世界”和“引进来”发展战略,提升现代化水准。应对中国销售市场的猛烈市场竞争,企业要灵活运用好国际性中国二种資源2个销售市场,提升国际化经营,推进经济发展技术协作。既要积极主动引入海外优秀技术,与国际性优秀企业沟通交流协作,还要灵活运用标准胆大走向世界开发设计国际市场。 3、钛白粉企业需变化营销战略,高度重视服务水平。现阶段绝大多数企业依然只关心于动能、耗能、成本指标上,欠缺深层次发掘客户满意度出示人性化服务。中国钛白粉企业应当勤奋贴近顾客、服务客户,乃至参加顾客的产品设计方案产品研发,并承担中后期的生产加工派送,完成服务项目外置,产生一条前后左右全线贯通的服务项目体制,提高企业运营保障体系,打造出优点知名品牌。 因而,钛白粉行业要成功渡过严冬,务必进一步完成技术自主创新、技术更新改造,从中低端产品开发设计市场销售变为开发设计高档技术产品,提升盐酸法钛白粉生产工艺流程,完成节能降耗、绿色经济的可持续发展观,提升企业竞争优势,积极推进行业转型升级,在挫折中存活发展趋势。 来源于:工程项目塑料在线 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |