牌号简介 About |
---|
Xenoy X4850树脂Xenoy X4850是一种水溶性、高模量、高韧性PC/PBT混合物。此外,该树脂具有高的耐化学性、极低的蠕变、低CTE、优异的脂肪和高的热尺寸稳定性。X4850可用于车身面板、安全设备、外壳、门把手、弹簧应用、医疗设备外壳、户外运动设备。 XENOY X4850 is a hydrostable, high modulus, high ductile PC/PBT blend. Furthermore, this resin provides high chemicalresistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. The X4850 could be positioned for body panels, safety equipment,housings, doorhandles, spring-loaded applications, medical device enclosures, outdoor sports equipment. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ASTM D792 |
密度 Density |
1.31 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
266℃,5.0kg 266℃,5.0kg |
4.5 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
265℃,5 kg 265℃,5 kg |
4.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.70 to 0.90 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 8 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
0℃ 0℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 9 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 9 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-20℃,Total Energy -20℃,Total Energy |
J | ASTM D3763 | |
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 11 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-30~80℃ TD:-30~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-30~80℃ MD:-30~80℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
|||
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/5 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 6 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 , 7 |
MPa | ISO 178 | |
弯曲强度 bending strength 5 |
|||
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | 内部方法 | |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,20 in/min |
3 类型 1, 0,20 in/min |
4 类型 1, 2,0 in/min |
5 0,051 in/min |
6 0,079 in/min |
7 Yield |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 80*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
2016军民两用先进碳资料论坛
2016-07-11 碳材料的发展和应用是提高军事实力与国防装备竞争力的重要因素之一,也已成为衡量一个国家科技水平、军事和经济实力是标志之一。石墨烯新材料,更因具有强度高、韧性好、重量轻、透光率高、导电性佳等特点,石墨烯材料将在国防军工领域扮演重要角色。为让大家了解碳材料方面协作配套的一些要求与标准、发展趋势与科技、应用与需求,北京新材料技术协会、中装国科(北京)新材料研究院、银基烯碳新材料股份有限公司、石墨邦决定于 2016年 |
2016军民两用先进碳资料论坛 碳材料的发展趋势和运用是提升军事力量与国防安全武器装备竞争能力的关键要素之一,也已变成考量一个国家高新科技水准、国防和经济实力是标示之一。石墨烯材料新型材料,更因具备抗压强度高、延展性好、重量较轻、透光度高、导电率佳等特性,石墨烯材料将在国防军工行业饰演关键人物角色。为让大伙儿掌握碳材料层面合作配套设施的一些规定与规范、发展趋向与高新科技、运用与要求,北京市新装饰材料技术研究会、上装国科(北京市)新型材料研究院、银基烯碳新材料股权有限责任公司、高纯石墨邦决策于 2016年8月16-18日在陕西省•西安市举办“军警民双用优秀碳材料社区论坛”,本次大会仍采用主会场展现与讨论紧密结合,讨论军用配套设施优秀碳材料发展趋势特性、网络热点,展现最近各种各样优秀碳材料技术性和商品,沟通交流优秀碳材料技术性与商品在国防安全行业的运用工作经验,推动军用配套设施优秀碳材料技术性的发展趋势,完成民俗科研成果的转换,另外推动军转民技术性的运用,会议内容为“发展趋势性能卓越、多运用、降低成本的军警民双用优秀碳材料”。大会期内将机构参观考察西安市新型材料高新科技展览馆。 一、大会议案以下:
1、石墨烯材料复合材料的研究及在军用行业的运用; 2、优秀碳材料LCA评定、检验点评和产品执行标准; 3、优秀碳材料服现役个人行为特点和特性评定; 4、废弃碳材料资源化再生收购 与运用; 5、优秀碳材料世界各国研究与产业链进度; 6、优秀碳材料在国防安全军械武器装备中的运用及规范; 7、优秀碳材料在陆海空武器装备中的运用及规范; 8、优秀碳材料建筑工程设计与模拟仿真研究; 9、新式碳材料在军用品零部件中的运用与取代; 10、性能卓越碳纤维材料在航天航空上的应用及规定; 11、碳纳米复合材料全新技术性研究与进度; 12、纳米碳管储能技术研究及在军用电子器件中的运用; 13、碳基复合材料先进工艺研究; 14、新式碳材料的表层改性材料以及运用; 15、泡沫塑料碳的全新研究及在军警民行业的运用; 二、参会目标
全部参会意味着将根据社区论坛主办方尤其邀约,参会意味着来源于武器制造商、军械武器装备制造商,科研院所、高校,优秀碳基复合材料、石墨烯材料复合材料、新式碳材料、性能卓越碳纤维材料、纳米碳管、泡沫塑料碳、纳米技术碳材料、优秀碳材料生产商,原材料检测公司等有关企业,热烈欢迎公司和政府部门冠名赞助。 保密性缘故当场禁止拍照,不与第三方共享资料。沒有被邀约的工作人员,不允许进到主会场,很感兴趣工作人员可提早与主办方联络。
三、会务费特定帐户 收费标准见申请表,协会理事参会请联络学术部(欲申请加入企业请索 函)。报名费用请汇至特定帐户。 账户名称:上装国科(北京市)新型材料研究院 开户行:农业银行北京市宣武分行业务部 银行账号: 1117 1101 0400 08202 四、主题活动官方网:www.bjxcx.org; 五、报考电話 手机上/手机微信: 13718204214、010-68669738、董灵杨; 传真电话:010-68669738; E_mail: donglingyang2008@163.com 来源于:中塑在线 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。