牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种软质、黑色、抗紫外辐射的热塑性硫化弹 性体(TPV)。这种材料同时具有良好的物理性质和耐化学性,适用于广泛的领域 。这一牌号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型、挤 出成型、吹塑成型、热成型或真空成型设备上加工。这是一种聚烯烃基材料,可在 生产过程中进行回收利用。 A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream. |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:TPV
用途:室外应用;汽车领域的应用;
颜色:黑色
加工条件:片材挤出成型,挤出吹塑成型,注吹成型,注射成型,热成型,真空成型,型材挤出成型,多次注射成型,共挤出成型 Extrusion,Injection Molding,Thermo forming,Profile extrusion,Multiple injection molding
性能特点: 可回收; 防火阻燃等级HB; 尺寸稳定性好; 耐疲劳性好; 耐化学性; 耐臭氧; 耐候抗UV; Renewable resources,Fatigue resistance,Solvent resistance,Ozone resistance,Good Dimensional Stability,Weather resistance is good,HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.968 | g/cm³ | ASTM D792 |
密度 Density |
0.970 | g/cm³ | ISO 1183 |
耐候性 Weathering resistance |
f1 | UL 746C | |
Detergent Resistance Detergent Resistance |
f4 | UL 2157 | |
Detergent Resistance Detergent Resistance |
f3 | UL 749 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
MPa | ISO 37 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
MPa | ASTM D412 | |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ASTM D412 | |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 37 | |
撕裂强度 tear strength |
|||
TD,23℃ TD,23℃ |
kN/m | ASTM D624 | |
TD,23℃ TD,23℃ |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 812 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.0 mm 1.0 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 在空气中(135℃,1008 hr) The rate of change in tensile strength in air (135 ℃, 1008 hr) |
% | ASTM D573 | |
拉伸强度的变化率 在空气中(135℃,1008 hr) The rate of change in tensile strength in air (135 ℃, 1008 hr) |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
135℃,1008 hr 135℃,1008 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(135℃,1008 hr) Change in Tensile Strain at Break in Air(135℃,1008 hr) |
% | ISO 188 | |
Change in Durometer Hardness in Air(邵氏 A,135℃,1008 hr) Change in Durometer Hardness in Air (135 ℃, 1008 hr) |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,135℃,1008 hr Shaw A, 135 ℃, 1008 hr |
ISO 188 | ||
拉伸强度的变化率 The rate of change in tensile strength |
|||
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ASTM D471 | |
Change in Tensile Stress(125℃,70 hr,in IRM 903 Oil) Change in Tensile Stress(125℃,70 hr,in IRM 903 Oil) |
% | ISO 1817 | |
Change in Ultimate Elongation(125℃,70 hr,in IRM 903 Oil) Change in Ultimate Elongation(125℃,70 hr,in IRM 903 Oil) |
% | ASTM D471 | |
Change in Tensile Strain at Break(125℃,70 hr,in IRM 903 Oil) Change in Tensile Strain at Break(125℃,70 hr,in IRM 903 Oil) |
% | ISO 1817 | |
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
耐连续最高温度 Durable to continuous maximum temperature |
|||
1008 hr 1008 hr |
℃ | SAE J2236 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
23 ℃,2 mm 23 ℃,2 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23 ℃,1.96 mm 23 ℃,1.96 mm |
IEC 60250 | ||
23 ℃,1.96 mm 23 ℃,1.96 mm |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高压电弧抗点燃指数(HVAR)(PLC) High voltage arc ignition resistance index (HVAR) (PLC) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.0 mm 1.0 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.00 mm 1.00 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 B 方法,直角形试样(割口) |
4 类型 1 |
5 类型 A |
【新闻资讯】查看全部
我国曾经成为世界塑料制品消费大国
2016-01-18 相对于金属、石材、木材,塑料制品具有成本低、可塑性强等优点,在国民经济中应用广泛,塑料工业在当今世界上占有极为重要的地位,多年来塑料制品的生产在世界各地高速度发展。 前瞻产业研究院发布的《2011-2015年中国塑料制品行业产销需求与投资预测分析报告》显示,我国塑料制品产量在世界排名中始终位于前列,其中多种塑料制品产量已经位于全球首位,我国已经成为世界塑料制品生产大国。2001-2010年我国塑料制品产量年均增幅维持在15%以上,2010年我国塑料制品总产量达到5830万吨 |
我国曾经成为世界塑料制品消费大国 相对性于金属材料、大理石、木料,塑料制品具备低成本、延展性强等优势,在社会经济中运用普遍,塑料工业在当今社会上占据极其重要的影响力,很多年来塑料制品的生产制造在世界各国高速运行发展。 展望产业研究院公布的《2011-2015年中国塑料制品行业产销需求与投资预测分析报告》显示信息,在我国塑料制品产量在全球排名中自始至终坐落于前端,在其中多种多样塑料制品产量早已坐落于全世界第一位,在我国早已变成全球塑料制品生产制造强国。2001-2010年在我国塑料制品产量年平均增长幅度保持在15%之上,2010年在我国塑料制品总产量做到5830万吨级。 塑料制品运用普遍,巨大的中下游行业为在我国塑料制品行业的发展出示了强大的支撑点。伴随着《振兴石化行业规划细则》的颁布,在我国塑料制品行业迈入新的发展机会。在我国塑料制品市场的需求关键集中化于农用机械塑料制品、包裝塑料制品、工程建筑塑料制品、工业生产交通出行及工程项目塑料制品等好多个层面。 展望产业研究院塑料制品行业研究者刘西妹表明,现阶段在我国平均塑胶消耗量与全球资本主义国家对比也有非常大的差别。做为考量一个国家塑料工业发展水准的指标值――塑钢型材比,在我国仅为30:70,不如全球均值的50:50,更远不如资本主义国家如英国的70:30和法国的63:37。将来伴随着在我国改性材料塑的技术性发展和消费理念升级,在我国塑料制品必须预估可维持10%之上的增长速度。 来源于:搜狐新闻 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。