牌号简介 About |
---|
Noryl RN0612是一种基于消费后循环(PCR)的可注射成型改性聚苯醚树脂,包含至少30%的PCR苯乙烯系列树脂含量。该树脂具有良好的尺寸稳定性和高流动性,还使用了非氯化、非溴化的FR添加剂,比密度为1.1 g/cm^3。Noryl RN0612可能是平板电视外壳应用的优秀材料候选,要求具有良好的流变性能、耐热性、抗水解性和低密度。 NORYL RN0612 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 30% PCR styrenic series resin content. Designed for good dimensional stability and high flow, this resin also uses non-chlorinated, non-brominated FR additives with a specific density of 1.1 g/cm^3. NORYL RN0612 may be an excellent material candidate for flat panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance and low density. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PPO(PPE)+PS PPO(PPE)+PS
用途:电视外壳;
加工条件:注射成型 Injection Molding
性能特点: 无卤; 防火阻燃等级V-1; 防火阻燃等级V-0; 尺寸稳定性好; 耐高温; 耐水解; 阻燃; 流动性高; 低密度; Good Dimensional Stability,High liquidity,Hydrolysis stability,Halogen free,Flame Characteristics,High Heat Resistance,Low density,V-1,V-0
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.11 | g/cm³ | ASTM D792, ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
300℃,1.2 kg 300℃,1.2 kg |
13.0 | cm³/10min | |
280℃,2.16 kg 280℃,2.16 kg |
34.0 | cm³/10min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
2100 | MPa | ASTM D638 |
-- -- |
2100 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 9 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 10 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 11 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 12 |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 13 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 14 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ASTM D1525, ISO 306/B50 10 15 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831, ISO 11359-2 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257,IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257,IEC 60093 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150,IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | ||
2 mm 2 mm |
℃ | ||
3 mm 3 mm |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*4 |
9 80*10*4 mm |
【新闻资讯】查看全部
三明氟化工产业步入展开的新阶段
2019-01-21 上周,福建省三明市工信局披露,当地一批氟化工产业重点项目目前进展顺利,产业正步入加快发展的新阶段。 福建三农新材料公司二期8000吨/年高品质聚四氟乙烯等含氟新材料项目于近期部分建成投产;福建清流县东莹化工公司扩建2万吨/年五氟乙烷项目也于近期建成试生产,新建3万吨/年R32生产线正在设备安装;三明市海斯福化工公司1万吨/年锂离子电解液等高端含氟精细化学品扩建项目正在设备安装;三明金氟化工科技公司2万吨/年氟钛酸钾、氟硼酸钾等项目已经建成投产;上市公司中欣氟材兼并重组福建高 |
三明氟化工产业步入展开的新阶段 上周,福建省三明市工信局披露,当地一批氟化工产业重点项目目前进展顺利,产业正步入加快发展的新阶段。 福建三农新材料公司二期8000吨/年高品质聚四氟乙烯等含氟新材料项目于近期部分建成投产;福建清流县东莹化工公司扩建2万吨/年五氟乙烷项目也于近期建成试生产,新建3万吨/年R32生产线正在设备安装;三明市海斯福化工公司1万吨/年锂离子电解液等高端含氟精细化学品扩建项目正在设备安装;三明金氟化工科技公司2万吨/年氟钛酸钾、氟硼酸钾等项目已经建成投产;上市公司中欣氟材兼并重组福建高宝矿业公司项目已发布公告,并完成资产评估等工作。另外,三明市已于近期新设立吉口循环经济产业园,首个落地项目福建三钢(集团)三明化工公司新建5万吨/年电子级氟化氢项目已经开工建设,主要生产设备完成招标采购工作。 来源:浙江省塑料行业协会 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- NORYL树脂光伏接线盒
- 2022-10-18 0
- NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度,长期在户外的湿热环境使用后,还可保持85%以上的性能,且具有低翘曲特性,满足对接线盒材料的高要求
- 阅读全文
NORYL树脂光伏接线盒
1-NORYL树脂具有优秀的尺寸稳定性、电气和热性能,能耐受-40°C至140°C的温度;
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
2-长期在户外的湿热环境使用后,可保持85%以上的性能;
3-具有低翘曲特性,满足对接线盒材料的高要求,如设计的灵活性、无氯无溴阻燃、易安装性等;
4-可降低系统成本,符合严格的全球监管标准。
收起
抱歉!暂无数据。