牌号简介 About |
---|
Lupolen 4261 AG是一种高分子量高密度聚乙烯(HDPE)。典型的客户应用包括汽车油箱应用。它以颗粒形式提供,并与挤出过程中的抗氧化剂一起稳定。该产品具有优异的抗环境应力开裂性能(ESCR),良好的耐化学性和良好的耐低温冲击性能。典型的工艺包括吹塑和热成型。Lupolen 4261 AG不适用于医疗和制药应用。该产品不能用于食品接触应用。 Lupolen 4261 AG is a high molecular weight high density polyethylene (HDPE). Typical customer applications include automotive fuel tank applications. It is supplied in pellets and is stabilized with antioxidants for the extrusion process. The product features an outstanding Enviromental Stress Cracking Resistance (ESCR), good chemical resistance in combination with an excellent low temperature impact resistance. Typical processes include blow moulding and thermoforming. Lupolen 4261 AG is not intended for use in medical and pharmaceutical applications. The product can not be used for food contact applications. |
产品描述 Product Description
厂家:荷兰利安德巴塞尔 LyondellBasell
类别:HMW-HDPE HMW-HDPE
用途:油箱;
加工条件:挤出吹塑成型
性能特点: 抗氧化; 耐化学性; 耐低温冲击; 高分子量; 冲击性能好; 抗应力开裂; High impact resistance,Inoxidizability,High molecular weight,Solvent resistance,low-temperature impact resistance,High ESCR
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.945 | g/cm³ | ISO 1183 , ASTM D1505 |
表观密度 Apparent density |
> 0.50 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
5.9 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
6.0 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
-- -- |
1000 | hr | ASTM D1693B |
F50 F50 2 |
hr | ASTM D1693B | |
100%非离子洗涤剂,F50 100% non-ionic detergent, F50 |
hr | ASTM D1693A | |
全切口蠕变试验 Full incision creep test 3 |
|||
3.5 MPa,80℃ 3.5 MPa,80℃ 3 |
day | ISO 16770 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 4 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
2% 正割,3.20 mm,50 mm跨距 2% secant, 3.20 mm, 50 mm span 5 , 6 |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服 yield 4 |
MPa | ASTM D790 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应变 Tensile strain 7 , 8 |
|||
屈服 yield |
% | ISO 527-2 | |
MD,断裂 MD, fracture 7 , 8 |
% | ASTM D882 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength |
ISO 8256/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 8256/1A | |
23℃ 23℃ |
kJ/m² | ISO 8256/1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
氧感应时间 Oxygen sensing time |
|||
200℃ 200℃ |
min | ISO 11357-6 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Igepal |
3 2% Arkopal N100 |
4 类型 4, 2.0 in/min |
5 方法 I (三点负荷), 0.51 in/min |
6 76x13x3.2 mm |
7 2.0 in/min |
8 Type IV |
【新闻资讯】查看全部
印度拟举行纯碱反倾销期中复审调查听证会
2016-02-24 印度商工部反倾销局近日发布公告,将于3月2日下午3点半在该局会议室举行纯碱(Soda Ash,税则号:283620)反倾销期中复审调查听证会。 印于2010年8月对上述产品发起反倾销调查,2012年2月发布肯定性终裁,建议对来自中国、欧盟、肯尼亚、巴基斯坦、伊朗、乌克兰和美国的上述产品征收反倾销税。 2015年7月21日,调查机关发起本次期中复审调查,倾销调查期为2014年4月至2015年3月。 |
印度拟举行纯碱反倾销期中复审调查听证会 印尼商工部反倾销局近日发布消息,将于3月2日中午6点半在各地各部门会议厅举办碳酸氢铵(Soda Ash,税则号:283620)反倾销其中复核调查听证制度。 印于2010年8月对所述商品发起反倾销调查,2012年2月公布具体性仲载,提议对来源于中国、欧盟国家、澳大利亚、塔吉克斯坦、沙特、俄罗斯和美国的所述商品征缴反倾销税。 2015年7月21日,调查行政机关发起此次其中复核调查,反补贴调查期是2014年4月至2015年3月。 来源于:国家商务部 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。