牌号简介 About |
---|
PET+PBT,40%玻璃纤维/矿物,注塑成型,改善流动性,高热尺寸稳定性 POCAN® T7141 000000 PET+PBT, 40 % glass fibers/mineral, injection molding, improved flowability, high thermal dimension stability POCAN® T7141 000000 PET+PBT, 40 % glass fibers/mineral, injection molding, improved flowability, high thermal dimension stability POCAN® T7141 000000 PET+PBT, 40 % glass fibers/mineral, injection molding, improved flowability, high thermal dimension stability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.70 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.90 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
280℃,2.16 kg 280℃,2.16 kg |
25.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:280℃,2.0 mm TD:280℃,2.0 mm 2 |
0.70 | % | ISO 2577 |
TD:120℃,2.0 mm,4 hrs TD:120℃,2.0 mm,4 hrs 3 |
0.10 | % | ISO 2577 |
MD:280℃,2.0 mm MD:280℃,2.0 mm 2 |
% | ISO 2577 | |
MD:120℃,2.0 mm,4 hrs MD:120℃,2.0 mm,4 hrs 3 |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲应变 Bending strain 5 |
% | ISO 178/A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 6 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 7792 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 110°C WZ, 600 bar |
3 60x60x2mm |
4 0.079 in/min |
5 2 mm/min |
6 10°C/min |
【新闻资讯】查看全部
警惕!你知道吗?塑料打包盒也会致人增肥
2016-02-15 在外面就餐吃不完往往要拿个塑料袋或塑料盒打包,但要小心,塑料制品中的邻苯二甲酸盐会增肥。邻苯二甲酸盐主要用于聚氯乙烯材料,使聚氯乙烯由硬塑料变得有弹性,不易破裂,起到增塑剂的作用。德国亥姆霍茨环境研究中心的研究人员发现,邻苯二甲酸盐进入人体会干扰新陈代谢,扰乱激素分泌,从而令人容易长胖。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |