一种黑色的、紫外线稳定的、无明显气味的再生树脂,用于与木粉混合,用于挤压装饰。通过添加增强填料和木粉分散剂,IMERPLASTTM 10WPCT可以显著提高挤出机的产量。熔化过滤至250微米,以确保无微粒。完全由Battenfeld Cincinnati和Wood K Plus批准 A black, UV stabilised, recycled resin with no significant odour, for compounding with wood flour for extruded decking applications. With added reinforcing filler and wood flour dispersant, ImerPlast TM 10WPCT has been shown to significantly improve extruder output. Melt filtered to 250 µm to ensure no particulates. Fully approved by battenfeld-cincinnati and Wood K Plus |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.40 | g/10min | |
230℃,5.0kg 230℃,5.0kg |
2.0 | g/10min | |
湿度 humidity |
0.1 | wt% | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
22.0 | MPa | |
弯曲模量 Bending modulus |
MPa | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Melt Filtration Melt Filtration |
µm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
聚碳酸酯/双酚A中国任务组启动
2015-12-16 12月14日,聚碳酸酯/双酚A中国工作组在全球工作组的框架下正式启动工作。该工作组隶属于中国石油和化学工业联合会,旨在提高公众对聚碳酸酯/双酚A的科学认知,客观认识双酚A(BPA)的化学性质,促进聚碳酸酯(PC)行业的健康发展。 中国石油和化学工业联合会会长李寿生表示,由于公众尚缺乏对BPA的科学认知,甚至存在误解,需要我们付出更多努力,提高公众认知,消除偏见和误解。聚碳酸酯/双酚A中国工作组的成立,正是在政府、科研机构、行业协会、企业和公众媒体间搭建公共平台,就PC和BP |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |