| 牌号简介 About |
|---|
| Fortus 3D生产系统Ultem 9085的生产级热塑性塑料是一种用于直接数字制造和快速成型的阻燃高性能热塑性塑料。由于其高强度重量比和FST（火焰、烟雾和毒性）等级，因此非常适合运输行业。这种独特的材料的现有认证使其成为商业运输行业的一个极好的选择-特别是航空航天，海洋和地面车辆。与Fortus 3D生产系统相结合，Ultem 9085允许设计和制造工程师生产完全功能性的零件，这些零件非常适合高级功能原型或最终用途，而无需传统工具的成本或交付周期。 Production-Grade Thermoplastic for Fortus 3D Production Systems ULTEM 9085 is a flame retardant high performance thermoplastic for direct digital manufacturing and rapid prototyping. It is ideal for the transportation industry due to its high strength-to-weight ratio and its FST (flame, smoke, and toxicity) rating. This unique material's preexisting certifications make it an excellent choice for the commercial transportation industry - especially aerospace, marine and ground vehicles. Combined with a Fortus® 3D Production System, ULTEM 9085 allows design and manufacturing engineers to produce fully functional parts that are ideal for advanced functional prototypes or end use without the cost or lead time of traditional tooling. |
产品描述 Product Description
用途：工程配件;汽车领域的应用;工业应用;航空航天应用;船舶应用;成型;模具;
颜色：黑色,棕黄色
加工条件：3D Printing, Fused Filament Fabrication (FFF)
性能特点： 防火阻燃等级V-0; 机械强度好; 经久耐用; 耐化学性; 易消毒; 耐高温; 阻燃; 冲击性能好; Good Rigidity,High impact resistance,Good disinfection,Flame Characteristics,High Heat Resistance,Durability,Solvent resistance,V-0
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.34 | g/cm³ | ASTM D792 |
|
Thickness（Layer Capability） Thickness（Layer Capability） |
254.0 到 330.2 | µm | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 3 |
|||
|
3.18 mm 3.18 mm 3 |
2220 | MPa | ASTM D638 |
|
拉伸强度 tensile strength 3 |
|||
|
3.18 mm 3.18 mm 3 |
71.7 | MPa | ASTM D638 |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂，3.18 mm Fracture, 3.18 mm 3 |
6.0 | % | ASTM D638 |
|
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
|
压缩模量 Compression modulus |
MPa | ASTM D732 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
|||
|
6.35 mm 6.35 mm |
MPa | ASTM D732 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
J/m | ASTM D256-A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ASTM E228 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电强度 Dielectric strength 5 , 6 |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant 6 |
ASTM D150 | ||
|
耗散因数 Dissipation factor 6 |
ASTM D150 | ||
|
体积电阻 Volumetric resistance 6 |
ohms | ASTM D257 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
FAA FAA |
FAR 25.853 | ||
|
NBS烟雾密度 NBS smoke density |
ASTM F814/E662 | ||
|
flaming flaming |
ASTM F814/E662 | ||
|
non-flaming non-flaming |
ASTM F814/E662 | ||
|
OSU总放热量 OSU total heat release |
FAR 25.853 | ||
|
2 min test 2 min test |
kW·min/m² | FAR 25.853 | |
|
5 min test 5 min test |
kW/m² | FAR 25.853 | |
|
垂直燃烧-60秒 Vertical combustion -60 seconds |
|||
|
1.02 到 6.35 mm 1.02 to 6.35 mm |
sec | FAR 25.853 | |
|
放热 exothermic |
|||
|
65/65，<40HR Peak，1.52 mm 65/65，<40HR Peak，1.52 mm |
FAR 25.853 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Outgassing Outgassing |
ASTM E595 | ||
|
Collected Volatile Condensable Material（CVCM） Collected Volatile Condensable Material（CVCM） |
% | ASTM E595 | |
|
Total Mass Lost（TML） Total Mass Lost（TML） |
% | ASTM E595 | |
|
Water Vapor Recovered（WVR） Water Vapor Recovered（WVR） |
% | ASTM E595 | |
|
抗真菌性 Antifungal activity |
|||
|
Method 508.6 Method 508.6 |
MIL STD-810G | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 类型 1, 0.20 in/min |
| 3 方法 I (三点负荷), 0.050 in/min |
| 4 方法A（短时间） |
| 5 All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
|
【新闻资讯】查看全部 
中国中化碳三项目首批装置启动试生产
2022-02-26 2月22日，位于中化连云港循环经济产业园的中国中化碳三项目首批装置启动试生产。 碳三项目首批试生产的装置包括年产15万吨环氧氯丙烷项目、年产18万吨环氧树脂项目、年产35万吨双 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付