PF-1聚偏氟乙烯薄膜由我公司专利(中国专利号201110048732.4)制得,是聚偏氟乙烯基纳米复合材料,白色不透明,机械强度高,热稳定性好,气体/液体渗透性低,阻燃性好,能有效分离和吸收紫外线,完全抗日光降解。具有优异的耐化学性和户外耐候性。酚醛型聚偏氟乙烯薄膜主要用作太阳能背面板涂层复合工艺中的表面基材。 PF-1 PVDF film be made by our company's patent (China patent no. 201110048732.4), it is the PVDF base nanocomposite, white color and opaque, with high mechanical strength, good thermal stability, low gas/liquids permeability, fire retardant, our PVDF film can effectively separate and absorb ultraviolet, completely sunlight degradation resistance, with excellent chemical resistance and outdoor weather durability. PF type PVDF film mainly used as surface substrate material in the solar back sheet of coating composite technology. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.81 到 1.85 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate 2 |
< 1.0 | % | ISO 11501 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
24 到 26 | µm | ISO 4593 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
> 30.0 | MPa | ASTM D882 |
TD,屈服 TD, yield |
> 30.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
UV透过率 UV transmittance |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 150°C for 30 min |
【新闻资讯】查看全部
2017年上海市塑料吸管产质量量监督抽查后果
2017-07-21 近期,上海市质量技术监督局组织相关质检机构对本市生产和销售的塑料吸管产品质量进行了监督抽查。共计抽查产品40批次,经检验,不合格0批次。 本次监督抽查依据GB9688-1988《食品包装用聚丙烯成型品卫生标准》等国家标准,对塑料吸管产品的下列项目进行了检测:感官、蒸发残渣、高锰酸钾消耗量、重金属(以Pb计)、脱色试验等。 具体抽查结果如下: 2017年上海市塑料吸管产品质量监督抽查所检项目符合相关标准的产品和企业名单 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |