牌号简介 About |
---|
KetaSpire® KT-880 GF30是高流量、30%玻璃纤维增强级聚醚醚酮(PEEK)。与未增强的KetaSpire PEEK树脂相比,该树脂具有更高的强度和刚度特性。增强材料在结构应用中也提供了更大的机械稳定性,特别是在工作温度接近300°C的情况下。KetaSpire Peek是按照最高行业标准生产的,具有独特的性能组合,包括优异的耐磨性、一流的抗疲劳性、以及熔融处理,纯度高,对有机物、酸和碱有良好的耐化学性。这些特性使其非常适合用于医疗、运输、电子、化学加工和其他工业用途。米色:kt-880 gf30 bg 20黑色:kt-880 gf30 bk 95 KetaSpire® KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. Beige: KT-880 GF30 BG 20 Black: KT-880 GF30 BK 95 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.53 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
400°C、2.16 kg 400°C、2.16 kg |
14 | g/10min | ASTM D1238 |
成型收缩率 Forming shrinkage rate |
|||
Flow:3.18 mm Flow:3.18 mm |
0.1-0.3 | % | ASTM D955 |
Across flow:3.18 mm Across flow:3.18 mm |
1.3-1.5 | % | ASTM D955 |
吸水率 Water absorption rate |
0.1 | % | ASTM D570 |
熔体表观粘度 Apparent viscosity of melt |
Pa·s | ASTM D3835 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
|
MPa | ASTM D638 | |
|
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
|
MPa | ISO 527-2 | |
|
MPa | ASTM D638 | |
断裂伸长率 elongation at break |
|||
|
% | ASTM D638 | |
|
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
|
MPa | ASTM D790 | |
|
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
|
MPa | ASTM D790 | |
|
MPa | ISO 178 | |
抗拉强度 tensile strength |
MPa | ASTM D695 | |
抗剪强度 Shear strength |
MPa | ASTM D732 | |
洛氏硬度 Rockwell hardness |
ASTM D-785 | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
J/m | ASTM D256 | |
|
KJ/m² | ISO 180/1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
J/m | ASTM D256 | |
|
KJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa 1.8 MPa |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
-50-50℃ -50-50℃ |
cm/cm/℃ | ASTM E831 | |
比热 specific heat |
|||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
3 mm 3 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
1 KHz 1 KHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
1 KHz 1 KHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.8 mm 0.8 mm |
UL 94 | ||
1.6 mm 1.6 mm |
UL 94 |
备注 |
---|
1 Passes 60s VB flame, smoke and toxicity requirements. |
2 Only KetaSpire® KT-880 GF30 BG20 is ISO 10993 certified |
3 一般属性:这些不能被视为规格。 |
4 5" x 0.5" x 0.125" |
5 0.20 in/min |
6 结晶 |
【新闻资讯】查看全部
福建联合石化公司新建装置一次开车成功
2021-07-25 搜料网资讯: 7月19日晚上10点,产品质量中心传来捷报,烷基化油产品辛烷值、馏程等指标均分析合格,满足专利商要求,标志着福建联合石化公司新建烷基化装置一次开车成功! 自烷 |
福建联合石化公司新建装置一次开车成功 搜料网资讯:7月19日晚上10点,产品质量中心传来捷报,烷基化油产品辛烷值、馏程等指标均分析合格,满足专利商要求,标志着福建联合石化公司新建烷基化装置一次开车成功! 自烷基化装置中交后,炼油二业务团队上下全面进入开工准备阶段,班组成员调整状态、整装出发,不遗余力投入到装置开车前的检查确认及各项准备工作中。团队定期开展三查四定销项例会,紧盯每一个问题项,严格把关、逐一销项。
装置吹扫气密期间,配套废酸再生装置还在施工,交叉作业多、现场风险大,团队成立开工党团突击队,上下齐心,统一思想,克服困难,确保安全有序完成开工准备。团队定期组织开展试车方案培训、事故应急演练、开车风险管控培训,确保开车安全工作落到实处。 7月18日16:00,烷基化反应器垫酸完成;23:00,烷基化反应器酸烃乳化完成;7月19日上午10:00,反应器引入碳四进料…… 在开工最关键阶段,炼油二业务团队管理人员与中石化开工专家组深入沟通研讨,进一步细化开工方案和应急预案,反复推演、优化流程环节,力保装置开工万无一失。 生产经理黄辉明和班组骨干连续几天几夜奋战在现场,昼夜坚守、有序衔接、严守规程,严格开工流程三级确认,确保试车工作稳步推进。随着各流程有序打通,烷基化装置按计划实现一次开车成功。 据悉,福建联合石化烷基化装置采用杜邦低温硫酸烷基化工艺,以碳四组分为原料生产不含烯烃、芳烃、馏程合理且饱和蒸气压低的高辛烷值汽油产品,是国六汽油产品良好的调和组分,提高了碳四的综合利用率。 烷基化装置是公司炼油产品结构调整及汽油产品品质升级项目的重要组成部分,将为炼油产品向高附加值产品转变迈出坚实的一步,对公司实现提质增效意义重大。 下一步,炼油二业务团队将继续发扬苦干实干、攻坚克难的精神,投入到废酸再生装置投料试车中去,坚决打赢开车攻坚战。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。