牌号简介 About |
---|
中等粘度,优异的阻燃性。紫外线稳定。清晰的色调和不透明的颜色。 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,I型,50 mm/min Fracture, Type I, 50 mm/min |
56 | MPa | ASTM D638 |
屈服,I型,50 mm/min Yield, Type I, 50 mm/min |
63 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,I型,50 mm/min Fracture, Type I, 50 mm/min |
90 | % | ASTM D638 |
屈服,I型,50 mm/min Yield, Type I, 50 mm/min |
7 | % | ASTM D638 |
弯曲强度 bending strength |
|||
屈服,1.30 mm/min,50 mm跨度 Yield, 1.30 mm/min, 50 mm span |
90.252 | MPa | ASTM D790 |
弯曲模量 Bending modulus |
|||
断裂,1.30 mm/min,50 mm跨距 Fracture, 1.30 mm/min, 50 mm span |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
泰伯磨损 Taber wear and tear |
|||
CS-17,1公斤 CS-17, 1 kg |
mg/1000cy | ASTM D1044 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
拉伸冲击 Tensile impact |
|||
S型 S-shaped |
cm-kgf/cm² | ASTM D 1822 | |
落镖冲击 Falling dart impact |
|||
D 3029,23℃ D 3029,23℃ |
cm-kgf | ASTM D 3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~40℃ MD:-30~40℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/℃ | ASTM C 177 | |
相对温度指数 Relative temperature index |
|||
非机械冲击性能 Non mechanical impact performance |
℃ | UL 746B | |
电气性能 Electrical performance |
℃ | UL 746B | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746B | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
ASTM D792 | ||
比容 Specific volume |
cm³/g | ASTM D 792 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
吸水率 Water absorption rate |
|||
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
平衡,100℃ Equilibrium, 100 ℃ |
% | ASTM D570 | |
收缩率 Shrinkage rate 5 |
|||
MD:3.2 mm MD:3.2 mm 5 |
% | 内部方法 | |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
g/10min | ASTM D1238 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
2.54 mm 2.54 mm |
% | ASTM D1003 | |
雾度 Haze |
|||
2.54 mm 2.54 mm |
% | ASTM D1003 | |
折射率 Refractive index |
ASTM D542 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
绝缘强度 Insulation strength |
|||
空气中3.2 mm 3.2 mm in air |
kV/mm | ASTM D 149 | |
相对电容率 Relative permittivity |
|||
50-60 Hz 50-60 Hz |
ASTM D150 | ||
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
50-60 Hz 50-60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
|||
钨丝 Tungsten wire |
PLC Code | ASTM D495 | |
热丝引燃{PLC} Hot wire ignition {PLC} |
PLC Code | UL 746A | |
高电压电弧起痕速率 {PLC} High voltage arc marking rate {PLC} |
PLC Code | UL 746A | |
高电流电弧引燃(表面{PLC}) High current arc ignition (surface {PLC}) |
PLC Code | UL 746A | |
相比漏电起痕指数 Compared to the leakage tracing index |
PLC Code | UL 746A | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
94V-2火焰等级 94V-2 flame level 3 |
mm | UL 94 | |
94V-0火焰等级 94V-0 flame level 3 |
mm | UL 94 | |
极限氧指数 Extreme oxygen index |
|||
LOI LOI |
% | ASTM D2863 | |
紫外线 ultraviolet radiation |
|||
水暴露/浸泡 Water exposure/soaking |
UL 746C |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
LG化学斥资2.6万亿韩元建设PBAT等工厂,年内开工
2021-08-20 搜料网资讯: 2021年8月19日,LG化学宣布:截至2028年将投资2.6万亿韩元(约143.65亿人民币),在忠清南道大山工厂建设生物降解PBAT和太阳能薄膜POE等共10家工厂。 今年年内开工建设的P |
LG化学斥资2.6万亿韩元建设PBAT等工厂,年内开工 搜料网资讯:2021年8月19日,LG化学宣布:截至2028年将投资2.6万亿韩元(约143.65亿人民币),在忠清南道大山工厂建设生物降解PBAT和太阳能薄膜POE等共10家工厂。 今年年内开工建设的PBAT工厂和POE工厂,预计年产能将分别达到5万吨和10万吨,两家工厂均计划于2024年投入商业化生产。预计由此产生的销售规模增长效应每年将超过4700亿韩元。 LG化学将以今年PBAT和POE工厂的开工建设为始点,计划截至2028年将大山工厂培育为生物基原料生产,环保材料、废塑料回收利用和温室气体减排等ESG项目的核心基地。
■ 截至2028年共建设生物降解PBAT和太阳能薄膜POE等10家工厂 - 生物基原料生产,环保材料、废塑料回收利用和温室气体减排等ESG项目的核心基地。 ■ 与忠清南道和瑞山市签署新项目和土地使用相关投资协议 - 大山第三产业园区内额外获得约79万平方米(24万坪)土地。 - 将助力直接或间接创造就业机会,振兴当地经济。 ■ CEO辛学喆副会长: "这项投资协议作为可持续发展战略的组成部分,预示着全面开展环保材料业务”。 "在加强与忠清南道和瑞山市的长期合作关系的基础上,将进一步提升合作水平,共同迈向可持续发展的未来”。 LG化学将在韩国进行大规模投资,用于培养石油化学领域的环保材料。将以高附加值的可持续发展项目和环保材料为中心,实现业务结构的全面转变。 据业内分析,在ESG趋势的蔓延下,随着可降解塑料的需求增加和新再生能源的扩大普及,到2025年PBAT和POE预计将以年均30%的速度快速增长。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。