牌号简介 About |
---|
PA 66,非增强,注塑,改善流动性,提高冲击强度,热老化稳定 Durethan® DP2325H3.0 000000 DUS031 (Dry) PA 66, non-reinforced, injection molding, improved flowability, improved impact strength, heat-aging stabilized Durethan® DP2325H3.0 000000 DUS031 PA 66, non-reinforced, injection molding, improved flowability, improved impact strength, heat-aging stabilized Durethan® DP2325H3.0 000000 DUS031 PA 66, non-reinforced, injection molding, improved flowability, improved impact strength, heat-aging stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm 2 |
0.30 | % | |
TD:280℃,2.0 mm TD:280℃,2.0 mm 3 |
1.7 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm 2 |
0.40 | % | |
MD:280℃,2.0 mm MD:280℃,2.0 mm 3 |
1.9 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ||
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ||
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ||
弯曲强度 bending strength 4 |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain 5 |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
|||
-30℃,冲击总贯穿能量 -30 ℃, total impact penetration energy |
J | ||
23℃,冲击总贯穿能量 23 ℃, total impact penetration energy |
J | ||
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
|||
-30℃ -30℃ |
N | ||
23℃ 23℃ |
N | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
熔融温度 Melting temperature 6 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 80°C MT, 600 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |
【新闻资讯】查看全部
欧盟达成对俄“禁油令”,自俄进口石油将被削减90%,俄最大银行被拉
2022-05-31 一夜之间,俄罗斯的石油和天然气出口均有重要变化。 当地时间30日晚,欧洲理事会主席米歇尔在社交媒体上表示,欧盟已就对俄实施石油禁运达成共识,将立即覆盖三分之二欧盟从俄 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |