牌号简介 About |
---|
低压建筑电线用低密度湿固化聚乙烯(UL型XHW-2、RHW-2、RHH、SIS、USE-2-UL“耐阳光”)Pexidan® X/T-UV2是一种低密度交联聚乙烯系统,可通过水分固化,由硅烷预接枝碱化合物A-3001和阻燃催化剂母粒CAT-047FR-UV2组成。以适当的比例(80:20)混合和挤压,这两种成分使材料在70-90°C热水或甚至环境湿度下固化。Pexidan® X/T-UV2是符合RoHS的系统。根据UL44,用该系统制造的绝缘材料可标记为所有颜色和所有尺寸的SUNRES。 Low density moisture curable polyethylene for ow voltage building wire and photovoltaic wire applications (UL styles XHHW-2, RHW-2, RHH, SIS, USE-2, and PV with SUNRES) PEXIDAN ® X/T-UV2 is a low density flame-retardant XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-047FR-UV2. Mixed and extruded in the proper proportions (80:20), the two components result in a material curable by exposure to 70-95°C hot water or even ambient moisture. PEXIDAN ® X/T-UV2 is halogenated but is RoHS-compliant. Insulation may be marked SUNRES or SR in all colors and in all sizes per UL44 and UL4703. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
67 | % | ASTM D2765 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
UL 1581 | ||
屈服 yield |
12.4 | MPa | |
断裂 fracture 1 |
13.6 | MPa | |
断裂 fracture 2 |
MPa | ||
断裂 fracture |
MPa | ||
断裂 fracture 3 |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | UL 1581 | |
断裂 fracture 5 |
% | UL 1581 | |
断裂 fracture |
% | UL 1581 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
老化测试 Aging test |
UL 1581 | ||
Elongation after exposure Elongation after exposure 6 |
% | ||
Elongation after exposure Elongation after exposure 7 |
% | ||
Original elongation Original elongation |
% | ||
Original tensile strength Original tensile strength |
MPa | ||
曝光后拉伸强度 Tensile strength after exposure 8 |
MPa | ||
曝光后拉伸强度 Tensile strength after exposure 9 |
MPa | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
变形 deformation |
% | UL 1581 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
100 MHz 100 MHz |
ASTM D150 | ||
90 ℃,60 Hz 90 ℃,60 Hz |
UL 1581 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 MHz 1 MHz |
|||
100 MHz 100 MHz |
|||
击穿电压 breakdown voltage |
UL 1581 | ||
-- -- |
V | ||
after glancing impact after glancing impact |
V | ||
绝缘电阻 insulation resistance |
UL 1581 | ||
23℃ 23℃ |
Mohms/1000 ft | ||
90℃ 90℃ |
Mohms/1000 ft | ||
after 12 weeks:90℃ after 12 weeks:90℃ |
Mohms/1000 ft | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
|||
4.0 mm 4.0 mm |
% | ASTM D2863 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
酸性气体排放 Acid gas emissions |
|||
HBr HBr |
% | CSA C22.2 No. 0.3 Method 2 | |
Crushing Test Crushing Test |
g | UL 1581 | |
高温伸长率 High temperature elongation 10 |
|||
负荷下伸长率,150℃ Elongation under load, 150 ℃ 10 |
% | 内部方法 | |
memo_intro memo_intro |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 After 60 day oil @ 75°C |
3 After 30 day gasoline @ 23°C |
4 After thermal ageing (7days @121°C) |
5 720 hr. exposure - SUNRES |
6 300 hr. exposure |
7 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
NatureWorks泰国新工厂获批,年产7.5万吨PLA
2021-08-11 搜料网资讯: 据统计,目前国内PLA主流厂家包括海正生物、安徽丰原等,未来数年新建/拟建PLA产能约为460万吨,十四五规划期间,海正生物计划投产15万吨,金丹科技计划投产20万吨, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |