牌号简介 About |
---|
鲁特-H XL1800是冲压式地暖饮用水管的理想材料。它是一种具有长期内压蠕变性能和交联性能、力学性能的优良产品。 Description LUTENE-H XL1800 is a optimum material for under-floor heating and tab-water pipe by RAM type extrusion. It is a excellent product with long-term internal pressure creep property and crosslinking property, mechanical properties. Applications Peroxide Crosslinked Pipes for Under-floor Heating and Drinking-water |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.950 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
2.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
8760 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
57 | ASTM D2240 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture |
3.43 | MPa | ASTM D638 |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
熔融温度 Melting temperature |
℃ | DSC |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.11 in/min |
4 压 力1 (10N) |
【新闻资讯】查看全部
改性塑料的概念与展开
2019-02-21 一、改性塑料的概念和发展 概念:塑料聚合物通过添加功能助剂、添加剂、填料等、或通过不同聚合物的共混,通过机械设备采用物理方法、化学方法或将不同的方法有机结合,制成符合一定要求的塑料聚合物。 改性技术:主要采用共混、填充、增韧、增强、相容、阻燃、合金化等技术,以提升树脂在阻燃性、耐老化、力学性能以及电、磁、光、热等方面的特性。 在通用塑料工程化、工程塑料高性能化基础上,改性塑料的生产过程也引入了纳米技术、凝聚态 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |