牌号简介 About |
---|
伊士曼TrTi共聚酯MP150是一种高流动性的伊士曼TrTIAN。伊士曼TrTi共聚酯MP150相对于伊士曼TrTi共聚酯MP100的粘度降低40%-50%。它用于挤压涂层工艺或需要高熔体流动速率的地方。其他突出的特点包括良好的韧性,水解稳定性,耐热性和耐化学性。伊士曼TrTITE共聚酯MP150可用于食品接触应用中的限制,符合USP 35<661>ISO1093和ISO11607的适用和选择部分。 Eastman Tritan copolyester MP150 is a high flow grade of Eastman Tritan. Eastman Tritan copolyester MP150 has viscosity reductions of 40-50% relative to Eastman Tritan copolyester MP100. It is intended for use in extrusion coating processes or where high melt flow rate is desirable. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan copolyester MP150 may be used in food contact applications with restrictions and is compliant with applicable and select sections of USP 35 <661>, ISO10993, and ISO11607. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ASTM D1505 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ASTM D955 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
130 | µm | |
弹性模量 Elastic modulus |
|||
MD,铸造薄膜 MD, cast thin film |
979 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
断裂 fracture |
52.0 | MPa | ASTM D638 |
屈服 yield |
MPa | ASTM D638 | |
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
MD,断裂,挤塑薄膜 MD, fracture, extruded film |
% | ASTM D882 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
ASTM D4812 | ||
23℃ 23℃ |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
|||
0.127 mm,铸造薄膜 0.127 mm, cast thin film |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
总计 total |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
塑料再生行业或是未来一个重点行业
2016-04-12 塑料再生行业就是捡塑料卖钱,而我们所说的再生塑料一般指消费后失去使用价值的可循环利用的塑料产品。但其实很多被弃置的旧塑料仍有它们的价格,只要经过回收、集中、分类、科学合理处置后就可以获得再生价值,实现循环利用。例如:PET塑料造成的水瓶,经回收和科学处理后,摇身一变,成了MisfitShine运动追踪器的时尚表带。 现今,我国的饮料瓶都尽量使用可回收材料和再生的材料,来增加材料的循环利用,节约全球资源。对塑料瓶进行回收再利用不仅能够解决环境污染问题,还能通过减少填埋量而减少 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |