牌号简介 About |
---|
Starflex GM1510BA是一种颗粒状的MLLDPE树脂,用于需要最大强度和韧性的应用场合。GM1210BA包含一个处理辅助装置,但不包含滑动或防阻塞装置。 Starflex GM1510BA is a pelletized mLLDPE resin for use in applications that require maximum strength and toughness. GM1210BA contains a processing aid but does not contain slip or antiblock. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.915 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
19 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:19 µm 1% secant, MD: 19 µ m |
172 | MPa | ASTM D882 |
1% 正割,TD:19 µm 1% secant, TD: 19 µ m |
186 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,19 µm MD, fracture, 19 µ m |
MPa | ASTM D882 | |
TD,断裂,19 µm TD, fracture, 19 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,19 µm MD, fracture, 19 µ m |
% | ASTM D882 | |
TD,断裂,19 µm TD, fracture, 19 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
19 µm 19 µm 2 |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:19 µm MD:19 µm |
g | ASTM D1922 | |
TD:19 µm TD:19 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,19.1 µm 45°,19.1 µm |
ASTM D2457 | ||
雾度 Haze |
|||
19.1 µm 19.1 µm |
% | ASTM D1003 |
备注 |
---|
2 F50 |
【新闻资讯】查看全部
其浓度已然超越海水 微塑料的危害正急剧添加
2016-08-03 回溯到2014年6月,首届联合国环境大会提出了海洋废弃物和微塑料的问题,并最终达成了“海洋塑料废弃物和微塑料决议”,提出开展有关海洋塑料废弃物和微塑料的研究,并提交给第二届联合国环境大会讨论。这一议题得到世界各国的广泛重视。时至今日,微塑料问题进展如何呢? 从近期相关报道中,我们找到了答案。由东京农工大学教授高田秀重等人组成的研究团队宣布,2000年以来,世界各地海底淤泥等沉积物中会造成海洋污染的塑料微粒子“微塑料”(MP)积蓄量急速增加,微塑料在淤泥中的浓度已超过海水。且 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |