牌号简介 About |
---|
CALIBRE™ 302-5 是一种应用于实体片材挤出的标准的线性聚碳酸酯树脂。CALIBRE™ 302-5 亦可用于加工不很复杂的多层壁结构,比如两层或者三层的片材。CALIBRE™ 302-5含有紫外线吸收剂添加剂,但是请注意室外应用的片材还需要一个防紫外线的保护层。建议使用CALIBRE™ 320UV进行共挤出,以制备出一个厚度为50 µm 的UV防护层。 主要特性: 优异的光学性能 抗冲击性能优异 耐热性能高 应用领域: 实体片材和多壁层片材 CALIBRE™ 302-5 is a standard linear polycarbonate resin designed for solid sheet extrusion. CALIBRE™ 302-5 is also suitable for the production of low complexity multi wall sheet, such as two and three wall sheet. CALIBRE™ 302-5 contains a UV absorber additive, but note that sheets for outdoor applications also require a protective UV cap layer. It is recommended to coextrude a 50 µm thick UV cap layer, using CALIBRE™ 320UV. Main Characteristics: Excellent optical properties Exceptional impact resistance High heat resistance Applications: Solid and multi-wall sheet applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ISO 1133 |
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ASTM D955 |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 2 |
% | ASTM D638 | |
屈服 yield 2 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser 5 |
% | ASTM D1044 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 6 | |
-- -- |
℃ | ASTM D1525 7 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A120 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 8 |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 方法 I (三点负荷), 0.079 in/min |
4 0.079 in/min |
5 CS10F 轮,250g,300 个周期 |
6 速率 A (50°C/h), 载荷2 (50N) |
7 标准 B (120°C/h), 压 力1 (10N) |
8 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
前3月中国肥料进出口量双降
2022-04-24 近日,中国海关分布的初步统计数据显示,1~3月,中国出口肥料415.5万吨,同比下降33.2%;进口243.6万吨,同比下降17%。 出口方面,1~3月,中国出口各种大量元素肥料(含氯化铵、硝酸 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |