CALIBRE™ 503-5 聚碳酸酯树脂具有较高的熔体强度,可以有效地对具有高达5层结构的低复杂程度至中等杂程度的多壁层结构进行定型。CALIBRE 503-5 这种聚碳酸酯树脂专门用于多壁层结构挤出加工。与诸如CALIBRE 302-5在内的标准的线性聚碳酸酯树脂相比,CALIBRE 503-5 是专为在较高速度的生产线制备更好的片材表面质量而研制的,而且更不易产生震痕。CALIBRE 503-5含有紫外线吸收剂,但是请注意室外用板材还需要一层吸收紫外线的保护层。推荐使用CALIBRE™ 320UV 与其共挤出,制造出一个厚度为50 micron的保护层。 主要特性: 熔体强度高: 低复杂程度至中等复杂程度的多壁层结构的加工 片材表面质量获得提升 优异的光学性能:减少震痕 应用领域: 多壁层结构片材 CALIBRE™ 503-5 Polycarbonate resin offers a high melt strength to calibrate effectively a wide range of multi-wall sheet structures from low to medium complexity, such as five wall sheet. CALIBRE 503-5 is a polycarbonate resin specially designed for multi-wall sheet extrusion. CALIBRE 503-5 is specially designed to offer a significantly better sheet surface quality at higher line speeds than a standard linear polycarbonate resin such as CALIBRE 302-5, and has a reduced tendency to display chatter marks. CALIBRE 503-5 contains a UV absorber additive, but sheets for outdoor applications require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 micron thick cap layer from CALIBRE 320UV. Main Characteristics: High melt strength: production of low to medium complexity multi-wall sheets Improved sheet surface quality Excellent optical properties: reduction in chatter marks Applications: Multi-wall Sheets |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ISO 1133 |
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ISO 294-4 |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 2 |
|||
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser 5 |
% | ASTM D1044 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | 内部方法 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 6 | |
-- -- |
℃ | ASTM D1525 7 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A120 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~80℃ MD:-40~80℃ |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 方法 I (三点负荷), 0.079 in/min |
4 0.079 in/min |
5 CS10F 轮,250g,300 个周期 |
6 标准 B (120°C/h), 压 力1 (10N) |
7 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
中国国际复合资料工业技术展览会
2018-09-06 彰显可持续发展,开创精彩世界 聚氨酯树脂让风力发电更高效 聚氨酯拉挤复合材料打造节能窗框 Desmocomp™树脂使太阳能组件边框更具可持续性 Maezio™复合材料让产品更加轻薄坚固 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |