牌号简介 About |
---|
3M Dyneon TFM改性聚四氟乙烯细粉TFM 2001Z是第二代乳液级聚四氟乙烯,适用于高性能管道和平垫圈应用。特殊特性符合ASTM D 4895 I型,1级,B类,由乳液聚合生产的高分子量聚四氟乙烯粉末。细粉末级,适用于中低压比(RR)范围内的烧结管各向同性机械性能,成功用作平垫圈的基本材料,具有良好的可焊性、化学惰性、光滑表面和高透明度、高抗应力开裂、耐冲击应力处理的高压。标准膏体挤出法低摩擦性能高阻燃性优异耐温性很好电性能 Dyneon™ TFM™ 2001 Z PTFE is an ideal grade for high-performance applications with reduction ratios up to 1000:1. This product has a denser polymer texture providing lower gas permeability than standard PTFE. Product Features: High molecular weight Isotropic mechanical properties Smooth surfaces and high transparency Very good weldability Emulsion polymerization PTFE High stress cracking resistance Meets ASTM D4895-04 Type 1, Grade 1, Class C classification High pressure resistance Processing by standard paste extrusion method |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.15 | g/cm³ | ISO 12086 |
表观密度 Apparent density |
0.46 | g/cm³ | ISO 60 |
平均颗粒尺寸 Average particle size |
520 | µm | ISO 13320 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
38.0 | MPa | ISO 527-3 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
440 | % | ISO 527-3 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
挤出压力 Extrusion pressure |
|||
Reduction Ratio 400 Reduction Ratio 400 |
MPa | ASTM D4895 | |
Reduction Ratio Reduction Ratio |
内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
印度计划出售ONGC公司1.5%股份
2022-03-31 据能源之声网站3月30日消息 根据交易所提交的一份文件,印度计划从周三开始通过要约出售,出售国有石油天然气公司至多1.5%的股份。 报价底价定为159卢比/股。政府的目标是从此次股 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-3M™ Dyneon™ TFM™ Modified PTFE TFM 2001Z证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)