牌号简介 About |
---|
Lumicene MPE M 1835是专为高性能铸造拉伸膜设计的,用于生产单层和多层膜。Lumicene MPE M 1835是一种以己烯为共聚单体的茂金属基低密度聚乙烯。LuMICEN MPE M 1835带来了高拉伸性(高达350%)在铸造拉伸膜突出的冲击和穿刺阻力极好的保持力非常好的加工能力在非常小的和大的铸造线非常低的凝胶级LuMICE MPE 1835也适用于其他应用如表面保护、食品包装、卫生膜和铸件。电影。与低密度聚乙烯(LDPE)和低密度聚乙烯(LLDPE)的共混性能良好。 Lumicene® mPE M 1835 is designed for high performance cast stretch film for mono and multilayer film production. Lumicene® mPE M 1835 is a Metallocene based Low Density Polyethylene with hexene as comonomer. Lumicene® mPE M 1835 brings: High stretchability (up to 350%) in cast stretch film Outstanding Impact and Puncture Resistance Excellent Holding Force Very good Processability on small and large cast lines Very low gel level Lumicene® mPE M 1835 is also suitable for other applications such as Surface Protection, Food Packaging, Hygiene Film and Cast Films. It exhibits an excellent blending-ability with LDPE and LLDPE was observed. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.5 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
拉伸强度 tensile strength |
|||
MD,屈服,20 µm,吹塑薄膜 MD, yield, 20 µ m, blow molded film |
7.00 | MPa | |
TD,屈服,20 µm,吹塑薄膜 TD, yield, 20 µ m, blow molded film |
6.40 | MPa | |
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
MPa | ||
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,20 µm,铸造薄膜 MD, fracture, 20 µ m, cast thin film |
% | ||
TD,断裂,20 µm,铸造薄膜 TD, fracture, 20 µ m, cast thin film |
% | ||
落锤冲击 Drop hammer impact |
|||
20 µm,铸造薄膜 20 µ m, cast thin film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:20 µm,铸造薄膜 MD: 20 µ m, cast thin film |
N | ||
TD:20 µm,铸造薄膜 TD: 20 µ m, cast thin film |
N | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ISO 14782 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
一文读懂!中国率先批准RCEP,化工行业将受何影响?
2021-03-25 搜料网资讯: 3月22日,商务部国际司负责人表示,目前,中国已经完成区域全面经济伙伴关系协定也就是RCEP协定的核准,成为率先批准协定的国家。此外,泰国也已经批准协定。RCEP所 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-TOTAL Polyethylene Lumicene® M 1835 (Cast Film)证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)