牌号简介 About |
---|
说明:Cosmic E4940P是一种矿物填充的玻璃增强环氧树脂模塑料,以颗粒形式提供。其特点是具有良好的尺寸稳定性,改进的热循环和卓越的防潮性。在150°C和1000 psi条件下,标准螺旋流量范围为25-35”(emmi)。它的热板凝胶时间为22-30秒,在160℃,182℃时为18-26秒,在5℃下保存八个月,适用于高质量的电阻网络和光纤连接器的封装,需要高质量、高可靠性和良好的成型性。 DESCRIPTION Cosmic E4940P is a mineral filled, glass reinforced epoxy molding compound which is supplied in a granular form. FEATURES It has excellent dimensional stability, improved thermal cycling and exceptional moisture resistance. Standard spiral flow range is 25-35" (EMMI) at 150°C and 1000 psi. It has a hot plate gel time of 22-30 seconds at 160°C, and 18-26 seconds at 182°C. It has a shelf life of eight months when stored at 5°C. APPLICATIONS It is designed for use in high-volume encapsulation of resistor networks and fiber-optic connectors requiring high quality, reliability and good moldability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.85 | g/cm³ | |
紧缩率 Shrinkage rate |
2.0 到 5.0 | ||
收缩率 Shrinkage rate |
|||
MD MD |
0.20 到 0.40 | % | |
吸水率 Water absorption rate 2 |
|||
平衡,50℃ Equilibrium, 50 ℃ 2 |
0.25 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
27 | J/m | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-- -- 3 |
cm/cm/℃ | ||
-- -- 4 |
cm/cm/℃ | ||
导热系数 Thermal conductivity coefficient |
W/m/K | ||
热变形温度 Hot deformation temperature |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ||
体积电阻率 Volume resistivity |
ohms·cm | ||
介电强度 Dielectric strength 5 |
|||
湿润 moist 5 |
kV/mm | ||
介电常数 Dielectric constant 6 |
|||
1 kHz 1 kHz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor 6 |
|||
1 kHz 1 kHz |
|||
1 MHz 1 MHz |
|||
耐电弧性 Arc resistance |
sec | ||
击穿电压 breakdown voltage |
|||
Wet Wet |
V | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
|||
拉伸强度 tensile strength |
MPa | ||
弯曲模量 Bending modulus |
MPa | ||
弯曲强度 bending strength |
MPa | ||
压缩强度 compressive strength |
MPa |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 48 hrs |
3 Alpha 1 |
4 Alpha 2 |
5 方法B(逐步) |
6 Wet |
【新闻资讯】查看全部
亨斯迈看好中国聚氨酯市场
2016-08-03 今日,全球领先的特殊化学品制造商亨斯迈携其新拓业务特诺 (Tecnoelastomeri)盛装亮相亚洲聚氨酯展览会 (UTECH Asia)暨2016中国国际聚氨酯展览会,这一展会是亚太地区最大的聚氨酯展览会之一。在本次展会上,亨斯迈聚氨酯事业部还携其热塑性聚氨酯 (TPU)业务、环氧丙烷/甲基叔丁基醚 (PO/MTBE)业务和在华合资企业宁武新材料 (NingWu)共同亮相,并推出多项创新产品和技术,专注于在汽车、鞋材、发泡材料的广泛应用,实践“构筑美好生活”的承诺。 作 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |