| 牌号简介 About |
|---|
| Lotr_ne q2018 H是在气相反应器中生产的乙烯-丁烯共聚物。它是为在大多数吹塑和铸膜应用中提供具有竞争力的性能而设计的。在为LLDPE设计的吹塑和流延薄膜机上，Lotr_ne Q2018 H可以在中等的挤出压力、良好的气泡稳定性和压力表控制下以较高的输出速率进行加工。Lotr_ne q2018 h可与吹塑和铸膜单挤出或共挤中使用的LDPE或其他PE树脂有利地混合，以改善薄膜性能。lotr_ne q2018 h适用于消费者、工业、食品或卫生包装领域的许多应用，如整理收缩、衬垫、填表密封、重型袋子、垃圾袋或其他袋子，以及农业薄膜（如隧道和覆盖膜）等非包装应用。 Lotrène ® Q2018 H is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most blown and cast film applications. Lotrène ® Q2018 H can be processed at high output rates with moderate extrusion pressure, good bubble stability and gauge control on blown and cast film machine designed for LLDPE. Lotrène ® Q2018 H can advantageously be blended with LDPE or other PE resins used in blown and cast film mono extrusion or coextrusion to improve film properties. Lotrène ® Q2018 H is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, liners, Form-Fill-Seal, heavy-duty sacks, refuse sacks or other bags and non-packaging applications like agricultural films e.g. tunnel and mulching films. |
产品描述 Product Description
用途：重包装袋;薄膜;衬里;包装;收缩性薄膜;袋子;食品包装;流延薄膜;吹膜;混合;农业应用;
加工条件：流延薄膜
性能特点： 抗结块性; 抗氧化; 高光滑性; 共聚物; 丁烯共聚单体; 良好的测量控制; 低密度; Smoothness,High anti-blocking,Good Gauge Control,Inoxidizability,Low density,Copolymer,Butylene copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
40 | µm | |
|
拉伸模量 Tensile modulus |
ISO 178 | ||
|
1% 正割，MD，40 µm，吹塑薄膜 1% secant, MD, 40 µ m, blow molded film |
215 | MPa | ISO 178 |
|
1% 正割，TD，40 µm，吹塑薄膜 1% secant, TD, 40 µ m, blow molded film |
245 | MPa | ISO 178 |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，40 µm，吹塑薄膜 MD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，屈服，40 µm，吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film 2 |
g | ISO 7765-1 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
|
MD：40 µm，吹塑薄膜 MD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
|
TD：40 µm，吹塑薄膜 TD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
|
熔融温度 Melting temperature |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，40.0 µm，吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
| 3 标准 B (120°C/h), 压 力1 (10N) |
|
【新闻资讯】查看全部 
共抗疫情 奥克集团全面复工
2022-04-10 为了全面打赢疫情防控阻击战，共同迎战疫情应对危机，全面服务和支持生产一线的员工，进一步加强安全生产，尽快恢复集团总部的正常工作，根据辽宁省人民政府《关于做好春节后 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付