牌号简介 About |
---|
EMERGE™ PC 8600 是一种阻燃、半透明的聚碳酸酯树脂。该树脂不含溴、氯或者磷酸盐添加剂,符合全球环保要求。这是一种易流动的PC树脂,适用于注塑加工。 应用领域: 信息技术设备 电源稳压器 EMERGE™ PC 8600 is a translucent ignition-resistant polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It is an easy flow PC resin suitable for use in injection molded applications. Applications: Information Technology Equipment Power adaptors |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
7.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
750 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 1 |
|||
23℃,3.20 mm,注塑,总能量 23 ℃, 3.20 mm, injection molding, total energy 1 |
58.8 | J | ASTM D3763 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
相对温度指数 Relative temperature index |
|||
电气性能,3.20 mm Electrical performance, 3.20 mm |
℃ | UL 746 | |
冲击机械性能,3.20 mm Impact mechanical performance, 3.20 mm |
℃ | UL 746 | |
3.20 mm 3.20 mm |
℃ | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 3 |
UL 94 | ||
1.50 mm 1.50 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index 4 |
|||
1.0 mm 1.0 mm 4 |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index 5 |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级,3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ||
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ||
弯曲模量 Bending modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 11.1 ft/sec |
3 标准 B (120°C/h), 压 力1 (10N) |
4 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
陶氏扩展AGILITY™高功能低密度聚乙烯树脂产品组合
2018-12-06 陶氏化学公司今日宣布扩大其AGILITY™高性能低密度聚乙烯(LDPE)树脂产品组合。新的树脂解决方案可以帮助薄膜制造商在中低线速度下实现轻量化涂布,以应对亚太地区的包装难题。 最新推出的AGILITYTM EC 7030高性能LDPE树脂采用陶氏的新型管式聚合专利技术,可满足亚太地区从高压釜式工艺向管式工艺转换的需求。该新产品进一步丰富了AGILITYTM产品组合,适用于不同速度的挤出机,可用于生产各类终端产品。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |