牌号简介 About |
---|
PETRONE GA501系列树脂是由客户选择的低密度聚乙烯颗粒衬里,用于薄膜挤出应用,需要良好的下拉和韧性。这些树脂具有优异的抗穿刺性、延伸率和热封强度。典型的应用包括重型运输袋,垃圾桶衬垫,商业和工业包装,以及食品和消费包装。 The Petrothene GA501 series of resins is pelletized linear low density polyethylene selected by customers for film extrusion applications that require excellent drawdown and toughness. These resins have excellent puncture resistance, elongation and heat seal strength. Typical applications include heavy duty shipping sacks, trash can liners, commercial and industrial packaging, as well as food and consumer packaging. GA501 is available without additives or fully formulated with slip and antiblock additives. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness 2 |
|||
测试 test 2 |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
193 | MPa | ASTM D882 |
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
186 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25.4 µm,吹塑薄膜 45 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blow-Up Ratio: 2.5:1 |
【新闻资讯】查看全部
科腾:业绩产品双双抢眼
2016-05-18 科腾(Kraton)――全球领先的苯乙烯嵌段共聚物、工程聚合物以及源自松木浆副产品的化学品生产商携最新特种聚合物盛大亮相CHINAPLAS,呈现了一份优异的成绩单。 在业绩方面,科腾同样表现不俗。2015年销售额接近10.4亿美元,公司与2016年1月6日完成对亚利桑那化学的收购工作。 目前科腾正在台湾麦寮建新的HSBC工厂。工厂建设预计在2016年第二季度完成,预定在2016年第四季度初开始试生产,总投资2亿美元,产能预计为每年3万吨 。HSBC主要有三个 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |