牌号简介 About |
---|
一种双组分高Tg透明环氧树脂,用于光纤电缆和组件的包装和组装。建议将光纤端接到金属箍中,或制作波导器件。它是EPO-TEK 353的快速固化替代品。符合美国药典第六类生物相容性标准。 A two component, high Tg, optically clear epoxy for packaging and assembly of fiber optics cables and components. It is suggested for termination of fibers into ferrules, or fabrication of waveguide devices. It is a faster curing alternative to EPO-TEK® 353ND. Complies with USP Class VI biocompatibility standards. |
技术参数 Technical Data | |||
---|---|---|---|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 5 |
1.570 | ||
透光率 Transmittance |
|||
700-1400 nm 700-1400 nm |
> 95.0 | % | |
1550 nm 1550 nm |
95.0 | % | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Degradation Temperature Degradation Temperature |
℃ | ||
Die Shear Strength(>10 kg,23℃) Die Shear Strength(>10 kg,23℃) |
MPa | ||
工作温度 working temperature |
|||
Continuous Continuous |
℃ | ||
Intermittent Intermittent |
℃ | ||
Storage Modulus(23℃) Storage Modulus(23℃) |
GPa | ||
加热减量 Heating reduction |
|||
200℃ 200℃ |
% | ||
250℃ 250℃ |
% | ||
300℃ 300℃ |
% | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 6 |
|||
-- -- 7 |
|||
密度 Density |
|||
Part B Part B |
g/cm³ | ||
Part A Part A |
g/cm³ | ||
粘度 viscosity 8 |
|||
23℃ 23℃ 8 |
Pa·s | ||
固化时间 Curing time |
|||
150℃ 150℃ |
hr | ||
储存稳定性 storage stability |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
搭接剪切强度 lap shear strength |
|||
23℃ 23℃ |
MPa | ||
相对电容率 Relative permittivity |
|||
1 kHz 1 kHz |
|||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature 2 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
-- -- 3 |
3.6E-5 | cm/cm/℃ | |
-- -- 4 |
1.7E-4 | cm/cm/℃ | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
|||
23℃ 23℃ |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
3 Below Tg |
4 Above Tg |
5 589 nm |
6 Part B |
7 Part A |
8 100 rpm |
【新闻资讯】查看全部
上海石化:生物可降解聚酯拓展海内市场
2016-05-24 日前,上海石化自主开发的无重金属环保型聚酯、生物可降解聚酯等新产品,亮相在美国波士顿举办的国际非织造布展览会,受到世界各地参展商关注。良好的知名度,得益于聚酯新产品早在2011年开始就走出国门,并在欧盟和俄罗斯等国拥有一席之地。 化工产品打开国际市场,一方面,可平衡国内化工产品过剩的局面,提升系统内工厂整体效益及开工率。另一方面,可通过与国际知名终端用户间的产品合作,提高产品质量档次,推进化工产品的转型升级。 近年来,上海石化金贸公司立足中国石化战略布局大力 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |