牌号简介 About |
---|
ARLEN™ A335是一种聚酰胺 6T(尼龙 6T)材料,含有的填充物为35% 玻璃纤维增强材料。 该产品在北美洲有供货,。 ARLEN™ A335的主要特性为:阻燃/额定火焰。 ARLEN™ A335 (Dry) ARLEN™ A335 is a Polyamide 6T (Nylon 6T) material filled with 35% glass fiber. It is available in North America. Primary attribute of ARLEN™ A335: Flame Rated. ARLEN™ A335 ARLEN™ A335 by Mitsui Chemicals is a modified polyamide 6T reinforced with 35% glass fiber. Possesses high dimensional stability, high melting point (320°C), minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance. Offers high rigidity even in a high-temperature atmosphere such as the inside of an engine room. Is suitable for processing by injection molding. ARLEN™ A335 is used in mechanical and structural applications including under the hood parts such as cooling system parts, cylinder head covers, thermostat cases, hydraulic system pistons and oil pump housings. Recommended for light-load tribological application parts of office automation equipment. Complies with UL 94 HB flame rating. Features: Possesses high dimensional stability, high melting point (320°C), minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance, and high rigidity. Applications: Mechanical and Structural parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.48 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
TD:2.0 mm TD:2.0 mm |
0.60 | % | ASTM D955 |
MD:2.0 mm MD:2.0 mm |
0.30 | % | ASTM D955 |
吸水率 Water absorption rate |
ASTM D570 | ||
23℃,24hr 23℃,24hr |
0.30 | % | ASTM D570 |
100℃,24hr 100℃,24hr |
1.8 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
熔融温度 Melting temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ASTM D696 | |
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
鑫达集聚会酰胺3D打印粉末耗材研发成功
2016-09-29 近日,鑫达集团研发团队成功完成了选择性激光烧结(SLS)聚酰胺粉末耗材的中试实验,以及材料的适配性验证,验证效果良好。至此,鑫达集团聚酰胺3D打印粉末耗材研发项目取得了圆满成功,为鑫达集团3D打印耗材家族再添一名新的成员。 新型聚酰胺3D打印粉末耗材研发的过程中,鑫达集团投入了大量的资金支持,研发人员秉持“精益求精,不断创新”的研发精神,通过不懈努力,反复试验和摸索,先后完成了新型聚酰胺粉末耗材配方设计,以及全新生产工艺的进一步优化,在已经完成的新型耗材小试实验的基础上,成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |