牌号简介 About |
---|
Elastollan® 1185AW是一种基于聚醚的热塑性聚氨酯(TPU),含有增塑剂。它是专门为电线和电缆、薄膜和片材以及挤压成型应用而设计的。它含有非卤化阻燃剂,在0.75、1.5和3.0 mm壁厚的垂直火焰试验中,其额定值为UL-94V-2。它还通过了FAR 25.853(a)火焰测试。它具有优异的耐磨性、韧性、透明度、低温柔韧性、水解稳定性和抗真菌性。它具有优良的阻尼特性和优异的抗撕裂扩展性能。Elastcollan1185a以未着色的颗粒形式提供。 Elastollan® 1185AW is a polyether-based thermoplastic polyurethane (TPU) containing a plasticizer. It is specifically formulated for wire and cable, film and sheet, and extruded profile applications. It contains a non-halogenated flame retardant and is rated UL-94 V-2 in vertical flame test for wall thicknesses of 0.75, 1.5 and 3.0 mm. It also passes FAR 25.853 (A) flame test. It exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1185A is supplied uncolored in pellet form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.16 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,3.80kg 190℃,3.80kg |
5.0 to 25 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
85 | ASTM D2240 | |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
19.3 | MPa | ASTM D412 |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
20.7 | MPa | ASTM D790 |
泰伯耐磨性 Taber abraser |
mg | ASTM D1044 | |
Abrasion(DIN) Abrasion(DIN) |
mm³ | DIN 53516 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | 内部方法 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
软化温度 Softening temperature |
|||
DMA DMA |
℃ | Internal Method | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
日本旭化成在德国新建控股企业
2016-03-17 旭化成在德国新建了旭化成欧洲股份有限公司,这是该公司在欧洲进行业务扩张,计划于2016年4月1日开始运行。 旭化成将对它在材料领域的三个核心业务公司,包括旭化成化学、旭化成纤维以及旭化成E-materials公司,进行合并,于2016年4月1日正式成为一个经营控股类企业。再加上旭化成微型装置公司,这些业务将组建成全新的旭化成材料业务,通过不同业务之间的强强联合,形成最大化的协同效应。 旭化成还将加强材料业务领域的市场营销以及产品提案能力,并以汽车应用为其业务 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |