牌号简介 About |
---|
氯丁橡胶是一种含抗氧化剂的丁烯共聚物线性低密度聚乙烯(C4-LLDPE),适用于高光学性能薄膜的挤出成型。主要应用flexirene cl 10被推荐用于生产手动和自动包装机中使用的拉伸膜。在多层膜中,flexirene cl 10增强了整体配方的光学性能;此外,由于其高加工性,建议在必须达到高生产率时使用树脂。 Flexirene CL 10 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for cast extrusion of thin film with high optical properties. Main Application Flexirene CL 10 is recommended for the production of stretch film to be used both in manual and in automatic wrapping machines. In a multilayer film, Flexirene CL 10 enhances the optical properties of the global formulation; moreover, for its high processability, the resin is recommended whenever high productivity has to be reached. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.8 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,铸造薄膜 With oneself - dynamic, casting thin films |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
23 | µm | |
薄膜厚度 film thickness |
10 to 50µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,23 µm,铸造薄膜 1% secant, MD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
1% 正割,TD,23 µm,铸造薄膜 1% secant, TD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,23 µm,吹塑薄膜 MD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,23 µm,吹塑薄膜 TD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,23 µm,吹塑薄膜 MD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,23 µm,吹塑薄膜 TD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,23 µm,铸造薄膜 MD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
TD,断裂,23 µm,铸造薄膜 TD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
23 µm,铸造薄膜 23 µ m, cast thin film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD:23.0 µm MD:23.0 µm |
kN/m | ISO 6383-2 | |
TD:23.0 µm TD:23.0 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,23 µm,铸造薄膜 45 °, 23 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
23 µm,铸造薄膜 23 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Cast Film |
【新闻资讯】查看全部
欧洲苯乙烯现货价钱飙升至4个半月高点
2018-01-25 据普氏能源资讯1月23日伦敦报道,根据标普全球普氏能源资讯公布的统计数据,欧洲苯乙烯现货价格日前飙升到了去年9月初以来的最高水平。 统计数据显示,欧洲苯乙烯5至30天远期现货价格在周一每吨猛增了80.5美元以后在周二每吨又暴涨了34美元,达到了每吨1462美元。 尽管盛禧奥公司在陶氏化学公司在相同地点的裂解装置出现问题以后在德国的Boehlen装置也出现了问题,欧洲苯乙烯市场上周一直相对平静。 尽管普氏能源无法确认具体细节,本周苯乙烯价格暴涨 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |