牌号简介 About |
---|
Xenoy HX5600HP是PBT基半结晶混合物,具有平衡流动和冲击性能。提高了对实验室消毒剂和化学品的耐化学性,用于医疗设备外壳和住房应用。卫生保健变化管理,生物相容性(ISO10993或USP六级)。ETO、伽马和蒸汽可灭菌。 Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
2100 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
2050 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
55.0 | MPa | ISO 527-2/50 |
断裂 fracture 3 |
52.0 | MPa | ASTM D638 |
屈服 yield 3 |
50.0 | MPa | ASTM D638 |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
|||
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 8 |
|||
-30℃ -30℃ 8 |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 9 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 9 |
|||
-40℃ -40℃ 9 |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 10 |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 11 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD MD |
ISO 11359-2 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ISO 11359-2 | |
23 到 60℃ 23 to 60 ℃ |
cm/cm/℃ | ISO 11359-2 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
g/10min | ASTM D1238 | |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
260℃,1500 sec^-1 260℃,1500 sec^-1 |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*4 sp=62mm |
8 80*10*3 sp=62mm |
9 80*10*4 |
10 80*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
九江石化聚丙烯装置各项目标均发明历史最好成绩
2016-12-14 九江石化化工运行部围绕提质增效总目标,多措并举,狠抓聚丙烯装置运行管理和节能降耗,装置长周期运行时间、装置产品产量、能耗指标均创造历史最好成绩。1~11月,运行部累计生产聚丙烯10.19万吨,提前超额完成年度生产任务,装置累计综合能耗和丙烯单耗等较公司年初下达指标分别降低3.58%和0.5%. 他们结合全年目标任务,在强化员工安全意识,加强现场巡检,积极消除设备隐患,努力提升聚丙烯装置运行平稳率的基础上,将各项能耗指标分解细化到班组,每月对班组能耗跟踪核算,并对完成情况进行 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |