牌号简介 About |
---|
ARLEN™ A315是一种聚酰胺 6T(尼龙 6T)材料,含有的填充物为15% 玻璃纤维增强材料。 该产品在北美洲有供货,。 ARLEN™ A315的主要特性为:阻燃/额定火焰。 ARLEN™ A315 (Dry) ARLEN™ A315 is a Polyamide 6T (Nylon 6T) material filled with 15% glass fiber. It is available in North America. Primary attribute of ARLEN™ A315: Flame Rated. ARLEN™ A315 ARLEN™ A315 by Mitsui Chemicals is a modified polyamide 6T reinforced with 15% glass fiber. Possesses high dimensional stability, high melting point (320°C), minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance. Offers high rigidity even in a high-temperature atmosphere such as the inside of an engine room. Is suitable for processing by injection molding. ARLEN™ A315 is used in mechanical and structural applications including under the hood parts such as cooling system parts, cylinder head covers, thermostat cases, hydraulic system pistons and oil pump housings. Recommended for light-load tribological application parts of office automation equipment. Complies with UL 94 HB flame rating. Features: Possesses high dimensional stability, high melting point (320°C), minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance. Offers high rigidity Applications: Mechanical and structural parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.30 | g/cm³ | ASTM D792 |
收缩率 Shrinkage Shrinkage rate |
|||
TD:2.0 mm TD:2.0 mm |
0.60 | % | ASTM D955 |
MD:2.0 mm MD:2.0 mm |
0.50 | % | ASTM D955 |
吸水率 Water Absorption Water Absorption |
ASTM D570 | ||
23℃,24hr 23℃,24hr |
0.40 | % | ASTM D570 |
100℃,24hr 100℃,24hr |
2.5 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass Transition Temperature Glass Transition Temperature |
℃ | DSC | |
熔融温度 Melting temperature Melting temperature |
℃ | ||
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
TD TD |
1/℃ | ASTM D696 | |
MD MD |
1/℃ | ASTM D696 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | ASTM D257 | |
介电强度 Dielectric Strength Dielectric Strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 Tensile Strength Tensile Strength |
MPa | ASTM D638 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk Broken BRK |
% | ASTM D638 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ASTM D790 | |
弯曲强度 Flexural Strength Flexural Strength |
MPa | ASTM D790 | |
洛氏硬度 Rockwell Hardness Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
近年来,我国环氧丙烷行业展开迅猛
2018-09-21 近年来,我国环氧丙烷行业发展迅猛, 预估2018年全年环氧丙烷国内总产量将达到280万吨以上,表观消费量有望突破300万吨。未来3-5年是国内环氧丙烷新增产能集中上马的时间段,如果计划内新增产能均能如期投产,预计到202 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |