牌号简介 About |
---|
高性能热塑性材料、无增强聚醚醚酮(PEEK)、半结晶、注射成型用深度过滤颗粒、非常容易流动、符合FDA食品接触标准、颜色自然/米色。具有更薄横截面或更长流动长度的复杂几何结构,具有高强度和刚度以及良好的延展性。耐腐蚀环境的化学性,适用于医疗和食品接触应用的灭菌。 High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, depth filtered granules for injection moulding, very easy flow, FDA food contact compliant, colour natural/beige. Complex geometries with thinner cross sections or longer flow lengths, for high strength and stiffness as well as good ductility. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
85 | ISO 868 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
4100 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
105 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
20 | % | ISO 527-2 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
3900 | MPa | ISO 178 |
弯曲强度 bending strength |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
125℃ 125℃ |
MPa | ISO 178 | |
175℃ 175℃ |
MPa | ISO 178 | |
275℃ 275℃ |
MPa | ISO 178 | |
压缩强度 compressive strength |
ISO 604 | ||
23℃ 23℃ |
MPa | ISO 604 | |
120℃ 120℃ |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
MD MD |
ISO 11359-2 | ||
< 143℃ < 143℃ |
cm/cm/℃ | ISO 11359-2 | |
> 143℃ > 143℃ |
cm/cm/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
ISO 22007-4 | ||
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
23℃ 23℃ |
W/m/K | ISO 22007-4 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
IEC 60093 | ||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
125 ℃ 125 ℃ |
ohms·cm | IEC 60093 | |
275 ℃ 275 ℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2.5 mm 2.5 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
23 ℃,1 kHz 23 ℃,1 kHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
ISO 4589-2 | ||
-- -- |
% | ISO 4589-2 | |
-- -- |
% | ISO 4589-2 | |
毒性 toxicity |
NES 713 | ||
CO content CO content |
NES 713 | ||
CO2 content CO2 content |
NES 713 | ||
Total gases Total gases |
NES 713 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
螺旋流动长度 Spiral flow length |
Internal Method | ||
-- -- |
cm | Internal Method | |
-- -- |
cm | Internal Method | |
-- -- |
cm | Internal Method | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
饱和,100℃ Saturation, 100 ℃ |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃ 400℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Crystalline |
3 1 mm |
4 模具温度: 320°F, 熔体温度: 689°F |
5 模具温度: 356°F, 熔体温度: 707°F |
6 模具温度: 392°F, 熔体温度: 752°F |
7 360°C nozzle |
8 at Yield |
9 200°C/4h |
10 Onset |
11 Average |
12 Along flow |
13 0.4 mm |
14 3.2 mm |
【新闻资讯】查看全部
巨化集团联合多家企业收购德国汉高EMC业务
2017-03-07 近日,巨化永利联合打造的新材料产业基金,首单跨国公司业务收购,最终高效率成功完成签约。 这是巨化集团携手优秀民营企业永利集团、央企中航国际旗下盛芯基金、上海领锐创投等合作伙伴,联合收购德国汉高集团EMC(环氧模塑料)业务100%股权以及相关知识产权、著名商标、研发资产和海内外营销渠道,进军半导体及大规模集成电路封装材料领域,共同发展新材料业务。 巨化集团董事长胡仲明出席签约仪式,并发表了热情洋溢的讲话。胡仲明表示,电子化学新材料是巨化“十三五”产业发展的重要 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |