牌号简介 About |
---|
Radel*R是聚苯砜(PPSU)的挤出形式,与其他非晶材料(包括聚砜和聚醚酰亚胺(PEI))相比,它具有更高的抗冲击性和更好的抗水解性。它保留了PEI的大部分热阻、稳定性和机械加工性。这些特性使其非常适合需要高压灭菌的医疗应用。 Radel R is an extruded form of polyphenylsulfone (PPSU) that offers higher impact resistance and has superior hydrolysis resistance than other amorphous materials, including both polysulfone and polyetherimide (PEI). It retains much of the thermal resistance, stability, and machinability of PEI. These properties make it ideal for medical applications requiring autoclaving. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.29 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
ASTM D570 | ||
24hr 24hr |
0.37 | % | ASTM D570 |
饱和 saturated |
1.1 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
130 | J/m | ASTM D256-A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
207 | ℃ | ASTM D648 |
最高使用温度 Maximum operating temperature |
|||
Long Term,Air Long Term,Air |
℃ | ||
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion 2 |
|||
MD:-40~149℃ MD:-40~149℃ 2 |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM F433 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 3 |
ohms | 内部方法 | |
介电强度 Dielectric strength 4 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
极限 limit |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
|||
10% 应变 10% strain |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
磨损因数 Wear factor |
10^-8 mm³/N·m | ASTM D3702 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 68°F |
3 EOS/ESD S11.11 |
4 方法A(短时间) |
【新闻资讯】查看全部
中国化工集团对山东公路集团施行战略重组
2018-01-16 中国化学工程集团有限公司成功完成对山东省公路建设(集团)有限公司的战略重组,日前已在济南举行山东公路集团战略重组签约仪式。据悉,本次战略重组完成后,中国化学工程集团有限公司及各股东方将通过资源嫁接、协同发展、优势互补,进一步释放山东公路建设集团的发展活力,提升核心竞争力,并推动企业积极“走出去”,参与到国家“一带一路”和区域协调发展战略中来。 记者了解到,中国化工集团去年以来资产整合提速的迹象越来越明显。2017年12月,天华院推出重组预案,拟以发行股份方式,合计作价约66 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |