牌号简介 About |
---|
Ryton® R-4XT和R-4-02XT 40%玻璃纤维增强聚苯硫醚化合物提供了增强的机械强度、良好的电气性能和优异的耐化学性,即使在高温下。 Ryton® R-4XT and R-4-02XT 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength with good electrical properties and outstanding chemical resistance, even at elevated temperatures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.69 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.20 | % | |
TD:3.2 mm TD:3.2 mm |
0.50 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.020 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
91 | J/m | ASTM D256 |
-- -- |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
J/m | ASTM D4812 | |
-- -- |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ASTM E831 | |
MD:100~200℃ MD:100~200℃ |
1/℃ | ASTM E831 | |
TD:-50~50℃ TD:-50~50℃ |
1/℃ | ASTM E831 | |
TD:100~200℃ TD:100~200℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ||
UL温度额定值 UL temperature rating |
℃ | UL 746B | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
25 ℃,1 kHz 25 ℃,1 kHz |
ASTM D150 | ||
25 ℃,1 MHz 25 ℃,1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
25℃,1 kHz 25℃,1 kHz |
ASTM D150 | ||
25℃,1 MHz 25℃,1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
绝缘电阻 insulation resistance 3 |
|||
90℃ 90℃ 3 |
ohms | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index 4 |
% | ASTM D2863,ISO 4589-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
-- -- |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 , ISO 527-2 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
泊松比 Poisson's ratio |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 95%RH, 48 hr |
3 ASTM D2863 is technically equivalent to ISO 4589-2. |
【新闻资讯】查看全部
2025年,全球注塑机市值估计复合增长率估计达3.5%
2019-01-23 根据Grand View Research研究机构的最近报道,到2025年,全球注塑机市值预计达到224.5亿美元,复合增长率达3.5%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |