牌号简介 About |
---|
PMC-T376J黑色酚醛树脂是一种两级、耐热/电成型材料,具有优异的模具加工能力和优化的固化周期。典型应用包括断路器、电气接线板、电信应用等。 PMC-T376J Black Phenolic is a two-stage, heat resistant/electrical molding material offering excellent mold process-ability and optimized Cure cycles. Typical applications include circuit breaker, electrical terminal strips, telecommunication application, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.56 | g/cm³ | ASTM D792 |
密度 Density |
1.56 | g/cm³ | JIS K7112 |
收缩率 Shrinkage rate |
|||
-- -- |
9.5 | % | JIS K6915 |
-- -- |
9.5 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.16 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
% | JIS K6911 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | JIS K6911 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | JIS K7203 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | JIS K6911 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁冲击强度 Charpy impact strength |
|||
-- -- |
kN/m | ASTM D256 | |
-- -- |
kN/m | JIS K7111 | |
悬臂梁冲击强度 Izod notched impact strength |
|||
-- -- |
kN/m | ASTM D256 | |
-- -- |
kN/m | JIS K6911 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | JIS K7207 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | JIS K6911 | |
介电强度 Dielectric strength |
|||
-- -- |
kV/mm | ASTM D149 | |
-- -- |
kV/mm | JIS K6915 | |
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
绝缘电阻 insulation resistance |
|||
-- -- 2 |
ohms | ASTM D257 | |
-- -- 2 |
ohms | JIS K6915 | |
-- -- 3 |
ohms | ASTM D257 | |
-- -- 3 |
ohms | JIS K6915 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.60 mm 0.60 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
贮藏期限 Storage period |
month |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 (N) |
3 (B) |
【新闻资讯】查看全部
Oliver-Tolas保健包装公司收购满加尔医疗包装
2016-05-16 近日Oliver-Tolas保健包装公司宣布收购满加尔医疗包装公司(Mangar Medical Packaging),该收购宣布自2016年5月10日起生效。 “在过去的30年里,满加尔医疗包装已经发展成为医疗包装行业内最受尊敬的公司之一。满加尔具备一流的制造能力、经验丰富的团队和服务客户的热情。我们非常高兴能够有机会将才华满意的满加尔团队收归麾下。”Oliver-Tolas.公司总裁兼首席执行官Jerry Bennish表示。 “我们计划将充分利用满加尔 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |