E210F是一种用于交联泡沫应用的伊娃(乙烯-醋酸乙烯酯共聚物)树脂,包括中底和运动鞋的鞋底。该等级产品设计用于在常规的捏合和轧制设备中混合和分散交联剂和发泡剂。 Description E210F is EVA resin for crosslinked foam applications including mid-sole and in-sole of athletic shoes. This grade is designed to be processed in conventional kneading and rolling equipment for mixing and dispersing crosslinking agent and foaming agent. Characteristics E210F offers good processability during compounding with various additives. Foamed products made from this grade provide excellent spilt tear resistance, superb tensile and elongation properties, and good compression set properties. Applications Athletic shoe mid-soles and in-soles, Sandals, Cushion padding |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.943 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.5 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
21.0 | wt% | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -70.0 | ℃ | ASTM D746 |
维卡软化温度 Vicat Softening Temp |
56.0 | ℃ | ASTM D1525 2 |
熔融温度 Melting temperature |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
南京海关查获走私废塑料二千余吨
2018-02-09 南京海关对外发布,2月7日凌晨,在该关成功打掉3个走私固体废物犯罪团伙,抓获主要犯罪嫌疑人12名,查证涉案走私固体废物废塑料2000余吨。 据了解,当天行动中,南京海关缉私局出动缉私警察104名,分成18个行动小组,在江苏、上海、广东、浙江等地同时开展查缉行动。南京海关初步侦查发现,2016年至今,3个走私犯罪团伙为谋取非法利益,采用借用他人许可证的方式,将涉案废塑料走私进境。涉案废塑料走私进境后,被违法转卖给无环保资质的企业,后者在加工、利用和销售过程中缺乏必要的污染防治 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |